Photosensitive resin composition for CTP flexographic printing original plate and printing original plate prepared therefrom

1. A photosensitive resin composition for CTP flexographic printing original plate containing

at least a hydrophobic polymer obtained from water-dispersible latex (A),

a hydrophilic polymer (B),

a photopolymerizable unsaturated compound (C)

a photopolymerization initiator (D), and

a rubber (E) for imparting rubber elasticity to the photosensitive resin composition, wherein the content of the rubber (E) is 1 to 7% by mass of the photosensitive resin composition,

characterized in that, the photopolymerizable unsaturated compound (C) comprises a photopolymerizable oligomer containing no hydroxyl group (C-1), a hydroxyl group-containing photopolymerizable monomer having a weight-average molecular weight of 200 to 1500 and having a pentaerythritol skeleton, a dipentaerythritol skeleton or a glycerol skeleton (C-2) and, a photopolymerizable monomer containing no hydroxyl group (C-3),

wherein the content of the hydroxyl group-containing photopolymerizable monomer (C-2) is 1 to 20% by mass of the photosensitive resin composition.

2. The photosensitive resin composition for CTP flexographic printing original plate according to claim 1 , wherein concentration of the hydroxyl groups derived from the hydroxyl group-containing photopolymerizable monomer (C-2) is 0.1 to 1.5 equivalent mol/kg.

3. The photosensitive resin composition for CTP flexographic printing original plate according to claim 1 , wherein concentration of the hydroxyl groups derived from the hydroxyl group-containing photopolymerizable monomer (C-2) is 0.1 to 1.5 equivalent mol/kg.

4. A CTP flexographic printing original plate, characterized in that, a heat-sensitive mask layer is formed on a surface of a photosensitive resin layer comprising the photosensitive resin composition mentioned in claim 1 .

5. A CTP flexographic printing original plate, characterized in that, a heat-sensitive mask layer is formed on a surface of a photosensitive resin layer comprising the photosensitive resin composition mentioned in claim 2 .

6. A CTP flexographic printing original plate, characterized in that, a heat-sensitive mask layer is formed on a surface of a photosensitive resin layer comprising the photosensitive resin composition mentioned in claim 3 .

7. A CTP flexographic printing original plate comprising the photosensitive resin composition according to claim 1 , and a support.

8. A CTP flexographic printing original plate according to claim 7 , wherein the support is formed of steel, aluminum, copper or nickel.

9. A CTP flexographic printing original plate according to claim 7 , wherein the support is formed of polyethylene terephthalate film, a polyethylene naphthalate film, a polybutylene terephthalate film or a polycarbonate film.

10. A CTP flexographic printing original plate according to claim 7 , wherein a heat-sensitive mask layer is formed on a surface of the photosensitive resin.

11. A CTP flexographic printing original plate according to claim 10 , wherein the CTP flexographic printing original plate further comprises a protective layer formed between the photosensitive resin layer and the heat-sensitive mask layer.

12. A CTP flexographic printing original plate according to claim 11 , wherein the protective layer is formed from a polymer selected from the group consisting of polyamide, polyvinyl alcohol, polyacrylic acid, polyethylene oxide, alkyl cellulose, hydroxypropyl cellulose, hydroxyethyl cellulose, nitrocellulose, cellulose acetate butyrate, polybutyral, butyl rubber, NBR rubber, acrylic rubber, styrene-butadiene rubber, latex or soluble polyester.