View Patent ↗The invention provides a lighting unit comprising a light source, configured to generate light source light and a particulate luminescent material, configured to convert at least part of the light source light into luminescent material light, wherein the light source comprises a light emitting diode (LED), wherein the particulate luminescent material comprises particles comprising cores, said cores comprising a phosphor comprising M′ x M 2-2x AX 6 doped with tetravalent manganese, wherein M′ comprises an alkaline earth cation, M comprises an alkaline cation, and x is in the range of 0-1, wherein A comprises a tetravalent cation, at least comprising silicon, wherein X comprises a monovalent anion, at least comprising fluorine, and wherein the particles further comprise a metal phosphate based coating, wherein the metal of the metal phosphate based coating is selected from the group consisting of Ti, Si and Al.
1. A lighting unit comprising;
a light source, configured to generate light source light; and
a particulate luminescent material configured to convert at least part of the light source light into luminescent material light,
wherein the light source comprises a light emitting diode (LED),
wherein the particulate luminescent material comprises particles comprising cores, said cores comprising a phosphor comprising M′ x M 2-2x AX 6 doped with tetravalent manganese, wherein M′ comprises an alkaline earth cation, M comprises an alkaline cation, and x is in the range of 0-1, wherein A comprises a tetravalent cation, at least comprising silicon, wherein X comprises a monovalent anion, at least comprising fluorine, and wherein the particles further comprise a metal phosphate based coating, wherein the metal of the metal phosphate based coating is selected from the group consisting of Ti, Si, and Al.
2. The lighting unit according to claim 1 , wherein the metal phosphate based coating comprises an aluminum phosphate coating.
3. The lighting unit according to claim 1 , wherein the particulate luminescent material is obtainable by contacting phosphor particles with a liquid comprising a precursor of the metal phosphate based coating, and wherein said liquid is obtainable by mixing an alcohol comprising liquid, a metal salt that is soluble in the alcohol comprising liquid, and a phosphate source, retrieving the thus treated phosphor particles, and drying the thus obtained treated phosphor particles to provide the particulate luminescent material.
4. The lighting unit according to claim 3 , wherein the phosphate source comprises P 2 O 5 .
5. The lighting unit according to claim 1 , wherein M′ x M 2-2x AX 6 comprises K 2 SiF 6 .
6. The lighting unit according to claim 1 , wherein the light source is configured to generate blue light.
7. A lighting unit comprising;
a light source, configured to generate light source light; and
a particulate luminescent material configured to convert at least part of the light source light into luminescent material light,
wherein the light source comprises a light emitting diode (LED),
wherein the particulate luminescent material comprises particles comprising cores, said cores comprising a phosphor comprising M′ x M 2-2x AX 6 doped with tetravalent manganese, wherein M′ comprises an alkaline earth cation, M comprises an alkaline cation, and x is in the range of 0-1, wherein A comprises a tetravalent cation, at least comprising silicon, wherein X comprises a monovalent anion, at least comprising fluorine, and wherein the particles further comprise a metal phosphate based coating, wherein the metal of the metal phosphate based coating is selected from the group consisting of Ti, Si, and Al,
wherein the particulate luminescent material further comprises one or more other phosphors selected from the group consisting of a divalent europium containing nitride luminescent material, a divalent europium containing oxynitride luminescent material, a trivalent cerium containing garnet, and a trivalent cerium containing oxynitride.
8. A method for the preparation of a particulate luminescent material which comprises particles comprising cores and a metal phosphate coating, wherein the cores comprise a phosphor comprising M′ x M 2-2x AX 6 doped with tetravalent manganese, wherein M′ comprises an alkaline earth cation, M comprises an alkaline cation, and x is in the range of 0-1, wherein A comprises a tetravalent cation, at least comprising silicon, wherein X comprises a monovalent anion, at least comprising fluorine, wherein the metal of the metal phosphate based coating is selected from the group consisting of Ti, Si, and Al, and wherein the method comprises:
contacting phosphor particles with a liquid comprising a precursor of the metal phosphate based coating,
mixing an alcohol comprising liquid, a metal salt that is soluble in the alcohol comprising liquid, and a phosphate source, to obtain said liquid,
retrieving the treated phosphor particles, and
drying the obtained treated phosphor particles to provide the particulate luminescent material.
9. The method according to claim 8 , wherein the metal of the precursor of the metal phosphate based coating comprises aluminum.
10. The method according to claim 8 , wherein the phosphate source comprises P 2 O 5 , and wherein the alcohol is a C2-C4 alcohol.
11. The method according to claim 8 , wherein M′ x M 2-2x AX 6 comprises K 2 SiF 6 .
12. The method according to claim 8 , wherein the phosphor particles are obtainable by a method comprising mixing a soluble salt of alkaline cation, a soluble salt of tetravalent manganese precursor, a tetravalent cation source, in an aqueous solution of an inorganic acid at least comprising HF, precipitating the phosphor, and drying the phosphor thus obtained, wherein the drying or any other optional later heat treatment process of the phosphor is performed at a temperature below 200° C.
13. The method according to claim 8 , wherein the alcohol comprises a C2-C4 alcohol.
14. The method according to claim 8 , wherein the particulate luminescent material further comprises one or more other phosphors selected from the group consisting of a divalent europium containing nitride luminescent material, a divalent europium containing oxynitride luminescent material, a trivalent cerium containing garnet, and a trivalent cerium containing oxynitride.
15. A particulate luminescent material which comprises particles comprising cores and a metal phosphate coating, wherein the cores comprise a phosphor comprising M′ x M 2-2x AX 6 doped with tetravalent manganese, wherein M′ comprises an alkaline earth cation, M comprises an alkaline cation, and x is in the range of 0-1, wherein A comprises a tetravalent cation, at least comprising silicon, wherein X comprises a monovalent anion, at least comprising fluorine, wherein the metal of the metal phosphate based coating is selected from the group consisting of Ti, Si and, Al.
16. The particulate luminescent material according to claim 15 , wherein M′ x M 2-2x AX 6 comprises K 2 SiF 6 and wherein the metal phosphate based coating comprises an aluminum phosphate coating.
17. The particulate luminescent material according to claim 15 , wherein the particulate luminescent material further comprises one or more other phosphors selected from the group consisting of a divalent europium containing nitride luminescent material, a divalent europium containing oxynitride luminescent material, a trivalent cerium containing garnet, and a trivalent cerium containing oxynitride.