Anti-filming surface-active agent
The invention relates to an anti-filming surface-active admixture for hydraulic binders, including at least one fatty alcohol and at least one oil, to the method for preparing same, and to a method for preparing a hydraulic binder composition suitable for the manufacture of screeds or concretes, comprising the step of adding, to the hydraulic binder composition, the admixture according to the invention in a metered amount of 0.1 to 5 wt % with respect to the weight of the hydraulic binder.
1. A method of making a hydraulic binder with improved resistance to formation of a surface film, the method consisting essentially of combining:
(a) at least one fatty alcohol,
(b) at least one oil, and
(c) the hydraulic binder,
wherein the hydraulic binder is more resistant to formation of the surface film compared to when the hydraulic binder is not combined with the at least one fatty alcohol and the at least one oil.
2. The method according to claim 1 , wherein the at least one fatty alcohol is in liquid form at room temperature.
3. The method according to claim 1 , wherein the fatty alcohol is a primary fatty alcohol.
4. The method according to claim 1 , wherein the fatty alcohol comprises 8 to 22 carbon atoms.
5. The method according to claim 4 , wherein the fatty alcohol is selected from the group consisting of hexadecan-1-ol, octadecan-1-ol and a mixture thereof.
6. The method according to claim 5 , wherein the at least one oil is a mineral oil, vegetable oil or a fatty acid ester of a vegetable oil.
7. The method according to claim 1 , wherein the at least one oil is an aliphatic, paraffinic or naphthenic mineral oil.
8. A The method according to claim 1 , wherein the mineral oil is a compound of formula C n H 2n+2 with n being between an integer between 8 and 30.
9. The method according to claim 1 , wherein the hydraulic binder is suitable for the production of screeds or concrete and wherein the at least one fatty alcohol and the at least one oil together constitute 0.1 to 5% by weight of the hydraulic binder.
10. A method of making a hydraulic binder with improved resistance to formation of a surface film, the method consisting essentially of combining:
(i) the hydraulic binder; and
(ii) an admixture comprising:
(a) at least one fatty alcohol,
(b) at least one oil, and
(c) a compound of formula (I),
RO(AO) n H (I)
wherein:
R is a hydrogen atom or an alkyl group, linear or branched, comprising 1 to 7 carbon atoms;
A is an alkylene, linear or branched, comprising 1 to 3 carbon atoms; and
n is an integer between 11 and 70, and
wherein the hydraulic binder is more resistant to formation of the surface film compared to when the hydraulic binder is not combined with the at least one fatty alcohol the at least one oil and the compound of formula I.
11. The method according to claim 10 , wherein the admixture comprises up to 99% by weight of a compound of formula (I), 0.5 to 99.5% by weight of a mineral oil and 0.5 to 30% by weight of a fatty alcohol, with respect to the total weight of the admixture.
12. The method according to claim 10 , wherein the admixture comprises 0 to 76% by weight of a compound of formula (I), 0.5 to 99% by weight of a mineral oil and 1 to 4% by weight of a fatty alcohol, with respect to the total weight of the admixture.
13. The method according to claim 10 , wherein the admixture is used at a proportion of 0.1 to 5% by weight with respect to the weight of the hydraulic binder.
14. The method according to claim 13 , wherein the screed is an anhydrite screed, a cement screed or a hemihydrate-based screed.
15. The method of claim 11 , wherein the hydraulic binder with improved resistance to formation of a surface film-comprises 0.5 to 15% by weight of a fatty alcohol, with respect to the total weight.
16. A method of forming a mortar screed, comprising pouring, setting and surface drying a hydraulic binder-based composition consisting essentially of:
a hydraulic binder;
at least one fatty alcohol; and
at least one oil
wherein the hydraulic binder is more resistant to formation of a surface film compared to when the hydraulic binder is not combined with the at least one fatty alcohol and the at least one oil.
17. A method of forming a mortar screed, comprising pouring, setting and surface drying a hydraulic binder-based composition consisting essentially of:
a hydraulic binder;
at least one fatty alcohol;
at least one oil; and
a compound of formula I:
RO(AO) n H (I),
wherein:
R is a hydrogen atom or an alkyl group, linear or branched, comprising 1 to 7 carbon atoms;
A is an alkylene, linear or branched, comprising 1 to 3 carbon atoms;
n is an integer between 11 and 70; and
wherein the hydraulic binder is more resistant to formation of a surface film compared to when the hydraulic binder is not combined with the at least one fatty alcohol and the at least one oil a compound of formula (I).