Method of measuring thickness of Fe—Zn alloy phase of galvannealed steel sheet and apparatus for measuring the same
View Patent ↗A method of measuring a thickness of a Fe—Zn alloy phase included in the Fe—Zn alloy coating of the galvannealed steel sheet includes: an X-ray irradiation process of irradiating the galvannealed steel sheet with the incident X-rays; and an X-ray detection process of detecting the diffracted X-rays obtained in the X-ray irradiation process, derived from a Γ·Γ 1 phase, a δ 1 phase, and a ζ phase included in the Fe—Zn alloy coating with a crystal lattice spacing d of 1.5 Å or higher.
1. A method of measuring a thickness of a Fe—Zn alloy phase of interest included in the Fe—Zn alloy phase of a galvannealed steel sheet, the method comprising:
an X-ray irradiation process of irradiating the galvannealed steel sheet with the incident X-rays; and
an X-ray detection process of detecting the diffracted X-rays, which are obtained in the X-ray irradiation process, derived from a Γ·Γ 1 phase, a δ1 phase, and a ζ phase included in the Fe—Zn alloy phase with a crystal lattice spacing d of 1.5 Å or higher,
wherein, in the X-ray detection process, a value obtained by subtracting a background intensity from an intensity of the diffracted X-ray with the crystal lattice spacing d corresponding to 1.507 Å, 1.536 Å, 1.623 Å, 1.720 Å, 1.833 Å, 1.899 Å, 1.914 Å, 1.971 Å, 2.363 Å, 2.593 Å, 2.770 Å, 3.692 Å, 4.109 Å, 5.535 Å, or 6.351 Å is used to measure the thickness of the Fe—Zn alloy phase of interest.
2. The method of measuring a thickness of a Fe—Zn alloy phase of the galvannealed steel sheet according to claim 1 ,
wherein, in the X-ray detection process, a thickness of the Γ·Γ 1 phase is measured using a value obtained by subtracting a background intensity from an intensity of the diffracted X-ray derived from the Γ·Γ 1 phase with the crystal lattice spacing d of 1.914 Å.
3. The method of measuring a thickness of a Fe—Zn alloy phase of the galvannealed steel sheet according to claim 1 or 2 ,
wherein, in the X-ray detection process, a thickness of the δ 1 phase is measured using a value obtained by subtracting a background intensity from an intensity of the diffracted X-ray derived from the δ 1 phase with the crystal lattice spacing d of 2.363 Å.
4. The method of measuring a thickness of a Fe—Zn alloy phase of the galvannealed steel sheet according to claim 1 or 2 ,
wherein, in the X-ray detection process, a thickness of the ζ phase is measured using a value obtained by subtracting a background intensity from an intensity of the diffracted X-ray derived from the ζ phase with the crystal lattice spacing d of 4.109 Å.
5. An apparatus used to measure a thickness of a Fe—Zn alloy phase of a galvannealed steel sheet, the apparatus comprising:
an X-ray tube; and
a detector which detects diffracted X-rays from the Fe—Zn alloy phase to measure an intensity of the diffracted X-ray,
wherein a diffraction angle between a direction of incident X-ray irradiated by the X-ray tube and a direction of the diffracted X-ray detected by the detector is an angle corresponding to a Γ·Γ 1 phase, a δ 1 phase, and a ζ phase included in the Fe—Zn alloy phase, and with a crystal lattice spacing d of 1.5 Å or higher, and wherein
the diffraction angle is an angle that corresponds to the crystal lattice spacing d of 1.507 Å, 1.536 Å, 1.623 Å, 1.720 Å, 1.833 Å, 1.899 Å, 1.914 Å, 1.971 Å, 2.363 Å, 2.593 Å, 2.770 Å, 3.692 Å, 4.109 Å, 5.535 Å, or 6.351 Å.
6. The apparatus used to measure a thickness of a Fe—Zn alloy phase of the galvannealed steel sheet according to claim 5 ,
wherein the diffraction angle is an angle that corresponds to the crystal lattice spacing d of 1.914 Å.
7. The apparatus used to measure a thickness of a Fe—Zn alloy phase of the galvannealed steel sheet according to claim 5 or 6 ,
wherein the diffraction angle is an angle that corresponds to the crystal lattice spacing d of 2.363 Å.
8. The apparatus used to measure a thickness of a Fe—Zn alloy phase of the galvannealed steel sheet according to claim 5 or 6 ,
wherein the diffraction angle is an angle that corresponds to the crystal lattice spacing d of 4.109 Å.
9. The apparatus used to measure a thickness of a Fe—Zn alloy phase of the galvannealed steel sheet according to claim 5 or 6 ,
wherein two or more of the detectors are included, and
the diffracted X-rays derived from at least two phases among the Γ·Γ 1 phase, the δ 1 phase, and the ζ phase are detected by the detectors.
10. The method of measuring a thickness of a Fe—Zn alloy phase of the galvannealed steel sheet according to claim 3 ,
wherein, in the X-ray detection process, a thickness of the ζ phase is measured using a value obtained by subtracting a background intensity from an intensity of the diffracted X-ray derived from the ζ phase with the crystal lattice spacing d of 4.109 Å.
11. The apparatus used to measure a thickness of a Fe—Zn alloy phase of the galvannealed steel sheet according to claim 7 ,
wherein the diffraction angle is an angle that corresponds to the crystal lattice spacing d of 4.109 Å.
12. The apparatus used to measure a thickness of a Fe—Zn alloy phase of the galvannealed steel sheet according to claim 7 ,
wherein two or more of the detectors are included, and
the diffracted X-rays derived from at least two phases among the Γ·Γ 1 phase, the δ 1 phase, and the ζ phase are detected by the detectors.
13. The apparatus used to measure a thickness of a Fe—Zn alloy phase of the galvannealed steel sheet according to claim 8 ,
wherein two or more of the detectors are included, and
the diffracted X-rays derived from at least two phases among the Γ·Γ 1 phase, the δ 1 phase, and the ζ phase are detected by the detectors.