Method for producing high-strength steel material excellent in sulfide stress cracking resistance
A steel has a chemical composition consisting of, by mass percent, C: 0.15-0.65%, Si: 0.05-0.5%, Mn: 0.1-1.5%, Cr: 0.2-1.5%, Mo: 0.1-2.5%, Ti: 0.005-0.50%, Al: 0.001-0.50%, and optionally at least one element selected from Nb: ≤0.4%, V: ≤0.5%, and B: ≤0.01%, Ca: ≤0.005%, Mg: ≤0.005%, and REM: ≤0.005%, and the balance of Fe and impurities, wherein Ni, P, S, N and O as impurities are Ni: ≤0.1%, P: ≤0.04%, S: ≤0.01%, N: ≤0.01%, and O: ≤0.01%. The steel is hot-worked into a shape and then sequentially subjected to heating the steel to a temperature exceeding the Ac 1 transformation point and lower than the Ac 3 transformation point and cooling. Then, a step of reheating the steel to a temperature not lower than the Ac 3 transformation point and quenching the steel by rapid cooling, and a step of tempering the steel at a temperature not higher than the Ac 1 transformation point are performed.
1. A method for producing a high-strength steel material excellent in sulfide stress cracking resistance, wherein a steel that has a chemical composition consisting of, by mass percent, C: 0.15 to 0.65%, Si: 0.05 to 0.5%, Mn: 0.1 to 1.5%, Cr: 0.2 to 1.5%, Mo: 0.1 to 2.5%, Ti: 0.005 to 0.50%, Al: 0.001 to 0.50%, and the balance of Fe and impurities, wherein Ni, P, S, N and O among the impurities are Ni: 0.1% or less, P: 0.04% or less, S: 0.01% or less, N: 0.01% or less, and O: 0.01% or less, and that has been hot-worked into a desired shape is sequentially subjected to the steps of the following [1] to [3]:
[1] a step of heating the steel to a temperature exceeding the Ac 1 transformation point and lower than the Ac 3 transformation point and cooling the steel;
[2] a step of reheating the steel to a temperature not lower than the Ac 3 transformation point and quenching the steel by rapid cooling; and
[3] a step of tempering the steel at a temperature not higher than the Ac 1 transformation point.
2. A method for producing a high-strength steel material excellent in sulfide stress cracking resistance, wherein a steel that has a chemical composition consisting of, by mass percent, C: 0.15 to 0.65%, Si: 0.05 to 0.5%, Mn: 0.1 to 1.5%, Cr: 0.2 to 1.5%, Mo: 0.1 to 2.5%, Ti: 0.005 to 0.50%, Al: 0.001 to 0.50%, at least one selected from the elements shown in (a) and (b), and the balance of Fe and impurities, wherein Ni, P, 5 , N and O among the impurities are Ni: 0.1% or less, P: 0.04% or less, S: 0.01% or less, N: 0.01% or less, and O: 0.01% or less, and that has been hot-worked into a desired shape is sequentially subjected to the steps of the following [1] to [3]:
[1] a step of heating the steel to a temperature exceeding the Ac 1 transformation point and lower than the Ac 3 transformation point and cooling the steel;
[2] a step of reheating the steel to a temperature not lower than the Ac 3 transformation point and quenching the steel by rapid cooling; and
[3] a step of tempering the steel at a temperature not higher than the Ac 1 transformation point;
(a) Nb: 0.4% or less, V: 0.5% or less, and B: 0.01% or less;
(b) Ca: 0.005% or less, Mg: 0.005% or less, and REM: 0.005% or less.
3. The method for producing a high-strength steel material excellent in sulfide stress cracking resistance according to claim 1 , wherein the steel having a chemical composition consisting of, by mass percent, C: 0.15 to 0.65%, Si: 0.05 to 0.5%, Mn: 0.1 to 1.5%, Cr: 0.2 to 1.5%, Mo: 0.1 to 2.5%, Ti: 0.005 to 0.50%, Al: 0.001 to 0.50%, and the balance of Fe and impurities, wherein Ni, P, S, N and O among the impurities are Ni: 0.1% or less, P: 0.04% or less, S: 0.01% or less, N: 0.01% or less, and O: 0.01% or less, is hot-finished into a seamless steel pipe and is air cooled, and thereafter is sequentially subjected to the steps of [1] to [3].
4. The method for producing a high-strength steel material excellent in sulfide stress cracking resistance according to claim 1 , wherein after the steel having the chemical composition consisting of, by mass percent, C: 0.15 to 0.65%, Si: 0.05 to 0.5%, Mn: 0.1 to 1.5%, Cr: 0.2 to 1.5%, Mo: 0.1 to 2.5%, Ti: 0.005 to 0.50%, Al: 0.001 to 0.50%, and the balance of Fe and impurities, wherein Ni, P, S, N and O among the impurities are Ni: 0.1% or less, P: 0.04% or less, S: 0.01% or less, N: 0.01% or less, and O: 0.01% or less, has been hot-finished into a seamless steel pipe, the steel is supplementarily heated at a temperature not lower than the Ar 3 transformation point and not higher than 1050° C. in line, and after being quenched from a temperature not lower than the Ar 3 transformation point, the steel is sequentially subjected to the steps of [1] to [3].
5. The method for producing a high-strength steel material excellent in sulfide stress cracking resistance according to claim 1 , wherein after the steel having the chemical composition consisting of, by mass percent, C: 0.15 to 0.65%, Si: 0.05 to 0.5%, Mn: 0.1 to 1.5%, Cr: 0.2 to 1.5%, Mo: 0.1 to 2.5%, Ti: 0.005 to 0.50%, Al: 0.001 to 0.50%, and the balance of Fe and impurities, wherein Ni, P, S, N and O among the impurities are Ni: 0.1% or less, P: 0.04% or less, S: 0.01% or less, N: 0.01% or less, and O: 0.01% or less, has been hot-finished into a seamless steel pipe, the steel is directly quenched from a temperature not lower than the Ara transformation point, and thereafter is sequentially subjected to the steps of [1] to [3].
6. The method for producing a high-strength steel material excellent in sulfide stress cracking resistance according to claim 4 , wherein the heating in step [1] is performed by a heating apparatus connected to an apparatus for quenching of inline heat treatment.
7. The method for producing a high-strength steel material excellent in sulfide stress cracking resistance according to claim 5 , wherein the heating in step [1] is performed by a heating apparatus connected to a quenching apparatus that performs direct quenching.
8. The method for producing a high-strength steel material excellent in sulfide stress cracking resistance according to claim 2 , wherein the steel has a chemical composition consisting of, by mass percent, C: 0.15 to 0.65%, Si: 0.05 to 0.5%, Mn: 0.1 to 1.5%, Cr: 0.2 to 1.5%, Mo: 0.1 to 2.5%, Ti: 0.005 to 0.50%, Al: 0.001 to 0.50%, at least one selected from the elements shown in (a) and (b), and the balance of Fe and impurities, wherein Ni, P, S, N and O among the impurities are Ni: 0.1% or less, P: 0.04% or less, S: 0.01% or less, N: 0.01% or less, and O: 0.01% or less,
(a) Nb: 0.4% or less, V: 0.5% or less, and B: 0.01% or less;
(b) Ca: 0.005% or less, Mg: 0.005% or less, and REM: 0.005% or less, is hot-finished into a seamless steel pipe and is air cooled, and thereafter is sequentially subjected to the steps of [1] to [3].
9. The method for producing a high-strength steel material excellent in sulfide stress cracking resistance according to claim 2 , wherein after the steel having the chemical composition consisting of, by mass percent, C: 0.15 to 0.65%, Si: 0.05 to 0.5%, Mn: 0.1 to 1.5%, Cr: 0.2 to 1.5%, Mo: 0.1 to 2.5%, Ti: 0.005 to 0.50%, Al: 0.001 to 0.50%, at least one selected from the elements shown in (a) and (b), and the balance of Fe and impurities, wherein Ni, P, S, N and O among the impurities are Ni: 0.1% or less, P: 0.04% or less, S: 0.01% or less, N: 0.01% or less, and O: 0.01% or less,
(a) Nb: 0.4% or less, V: 0.5% or less, and B: 0.01% or less;
(b) Ca: 0.005% or less, Mg: 0.005% or less, and REM: 0.005% or less, has been hot-finished into a seamless steel pipe, the steel is supplementarily heated at a temperature not lower than the Ar 3 transformation point and not higher than 1050° C. in line, and after being quenched from a temperature not lower than the Ar 3 transformation point, the steel is sequentially subjected to the steps of [1] to [3].
10. The method for producing a high-strength steel material excellent in sulfide stress cracking resistance according to claim 2 , wherein after the steel having the chemical composition consisting of, by mass percent, C: 0.15 to 0.65%, Si: 0.05 to 0.5%, Mn: 0.1 to 1.5%, Cr: 0.2 to 1.5%, Mo: 0.1 to 2.5%, Ti: 0.005 to 0.50%, Al: 0.001 to 0.50%, at least one selected from the elements shown in (a) and (b), and the balance of Fe and impurities, wherein Ni, P, S, N and O among the impurities are Ni: 0.1% or less, P: 0.04% or less, S: 0.01% or less, N: 0.01% or less, and O: 0.01% or less,
(a) Nb: 0.4% or less, V: 0.5% or less, and B: 0.01% or less;
(b) Ca: 0.005% or less, Mg: 0.005% or less, and REM: 0.005% or less, has been hot-finished into a seamless steel pipe, the steel is directly quenched from a temperature not lower than the Ar 3 transformation point, and thereafter is sequentially subjected to the steps of [1] to [3].