Cutting tool
A cutting tool includes a substrate composed of a cermet. The cermet includes a hard phase including compounds containing Ti, at least one metal other than Ti selected from groups 4, 5, and 6 of the periodic table, and at least one element of carbon and nitrogen, a binder phase including, as a main component, an iron group metal, and unavoidable impurities. At least one type of particles selected from alumina particles and zirconia particles with an average particle size of 0.5 μm or more and 5 μm or less is scattered over a surface of a rake face of the substrate, and the concentration of at least one element of aluminum and zirconium in the surface is 0.5 at % or more and 5 at % or less.
1. A cutting tool comprising a substrate composed of a cermet, wherein
the cermet includes a hard phase including compounds containing Ti, at least one metal other than Ti selected from groups 4, 5, and 6 of the periodic table, and at least one element of carbon and nitrogen, a binder phase including, as a main component, an iron group metal, and unavoidable impurities, wherein at least one type of particles selected from alumina particles and zirconia particles with an average particle size of 1 μm or more and 4 μm or less is scattered over a surface of a rake face of the substrate, and the concentration of at least one element of aluminum and zirconium in the surface is 1 at % or more and 2.5 at % or less.
2. The cutting tool according to claim 1 , wherein the average hardness in a region from a sintered surface of the surface of the substrate to a depth of 50 μm is 10% or more higher than the average hardness in a region in the depth range of 150 to 200 μm from the sintered surface.
3. A cutting tool comprising a substrate composed of a cermet, wherein
the cermet includes a hard phase including compounds containing Ti, at least one metal other than Ti selected from groups 4, 5, and 6 of the periodic table, and at least one element of carbon and nitrogen, a binder phase including, as a main component, an iron group metal, and unavoidable impurities, wherein
at least one type of particles selected from alumina particles and zirconia particles with an average particle size of 0.5 μm or more and 5 μm or less is scattered over a surface of a rake face of the substrate, and the concentration of at least one element of aluminum and zirconium in the surface is 0.5 at % or more and 5 at % or less, and
the average hardness in a region from a sintered surface of the surface of the substrate to a depth of 50 μm is 10% or more higher than the average hardness in a region in the depth range of 150 to 200 μm from the sintered surface.
4. The cutting tool according to claim 3 , wherein the average particle size of at least one type of particles selected from alumina particles and zirconia particles is 1 μm or more and 4 μm or less.
5. The cutting tool according to claim 3 , wherein the concentration of at least one element of aluminum and zirconium is 1 at % or more and 2.5 at % or less.