Composite panels usefully employed in anti-ballistic products and methods to make the same
Composite panel comprising at least one layer containing at least one tape comprising a thermoplastic polymer selected from the group consisting of polyolefins, polyesters, polyvinyl alcohols, polyacrylonitriles, polyamides or polyketone, wherein the tape has a tensile strength of at least 1.2 GPa and an areal density of between 5 and 150 g/m 2 , and an adhesive in contact with said layer, whereby the amount of the adhesive in contact with one side of the at least one layer is between 0.2 and 15 g/m 2 , wherein the adhesive is a plastomer wherein said plastomer is a random copolymer of ethylene or propylene and one or more C 2 to C 12 a-olefin co-monomers and wherein said plastomer has a density as measured according to 1801183 of between 860 and 930 kg/m 3 . In a preferred embodiment the tape comprises an ultra high molecular weight polyethylene. The composite panel is used in a ballistic resistant article.
1. A composite panel comprising at least four tape layers, wherein
each of the tape layers comprises at least one tape comprising a thermoplastic polymer selected from the group consisting of polyolefins, polyesters, polyvinyl alcohols, polyacrylonitriles, polyamides and polyketone, wherein the at least one tape has a tensile strength of at least 1.2 GPa and an areal density of between 5 and 250 g/m 2 , and
between 0.2 and 15 g/m 2 of an adhesive in contact with the at least one tape layer, wherein
the adhesive is a plastomer and wherein the plastomer is a random copolymer of ethylene or propylene and one or more C 2 to C 12 α-olefin co-monomers, and wherein the said plastomer has a density as measured according to ISO1183 of between 860 and 930 kg/m 3 , and wherein
the composite panel has an areal density between 0.25 Kg/m 2 and 250 Kg/m 2 .
2. The composite panel of claim 1 , wherein the at least one tape comprises a polyolefin.
3. The composite panel of claim 1 , wherein the at least one tape in the tape layers is unidirectionally aligned or woven.
4. The composite panel of claim 1 , wherein the tape layers comprise a plurality of unidirectionally aligned tapes, wherein a direction of orientation of the tapes in one layer comprising the unidirectionally aligned tapes is at an angle β relative to a direction of orientation of the tapes in an adjacent layer, and wherein β is between 5 and 90°.
5. The composite panel of claim 1 , wherein the random copolymer in the panel is present in an amount of less than 15 wt %.
6. The composite panel of claim 1 , wherein the panel comprises at least eight tape layers, and wherein each of the tape layers comprises the at least one tape.
7. The composite panel of claim 1 , wherein the panel has an areal density between 0.5 Kg/m 2 and 100 Kg/m 2 .
8. The composite panel of claim 1 , wherein the adhesive is heterogeneously distributed over the at least one tape layer so as to establish areas of the at least one tape layer having no adhesive.
9. The composite panel of claim 8 , wherein the adhesive layer is a web-like structure.
10. The composite panel of claim 1 , wherein the adhesive is inhomogeneously in contact with the at least one tape layer so as to establish areas having respective lower and higher amounts of the adhesive.
11. A product which comprises the composite panel of claim 1 , wherein the product is selected from the group consisting of ballistic resistant articles, armor, vehicles, buildings, radomes and building components.
12. A ballistic resistant article which comprises the composite panel according to claim 1 .
13. A method of making the composite panel of claim 1 , the method comprising:
(a) providing the at least four tape layers, wherein each of the tape layers comprises at least one tape comprising a thermoplastic polymer selected from the group consisting of polyolefins, polyesters, polyvinyl alcohols, polyacrylonitriles, polyamides and polyketone, wherein the tape has a tensile strength of at least 1.2 GPa and an areal density of between 5 and 250 g/m 2 , and a plastomer
(b) stacking the at least one layer and the plastomer to form an assembly thereof;
(c) compressing the thus formed assembly at a pressure of at least 0.1 MPa and a temperature between 10° C. above the melting temperature of the plastomer and the melting temperature of the tape, wherein
the plastomer in the assembly is in contact with the at least one layer, and wherein the plastomer is a random copolymer of ethylene or propylene and one or more C 2 to C 12 α-olefin co-monomers, and wherein said plastomer has a density as measured according to ISO1183 of between 860 and 930 kg/m 3 ; and wherein the plastomer in contact with one side of the at least one layer is present in an amount between 0.2 and 15 g/m 2 .
14. The method according to claim 13 , wherein the plastomer provided in step (a) is in a form of a powder, a film, a tape, a dispersion, a solution, an emulsion, a hot melt, or a carrier sheet comprising the plastomer.
15. The method according to claim 13 , wherein the at least four tape layers and the plastomer provided in step (a) of the process are in a form of a sheet comprising the at least one layer and the plastomer in contact with the at least one layer.
16. The method according to claim 15 , wherein step (a) comprises providing a sheet comprised of the at least four tape layers and the plastomer.
17. The method of claim 16 , wherein the at least four tape layers comprise a plurality of unidirectionally aligned tapes or at least one layer of a plurality of woven tapes.
18. The method according to claim 16 , wherein the sheet is a composite tape comprised of the at least one tape and the plastomer.