Polyester resin, resin composition for can paint, painted metal plate for can, and can
This invention provides a polyester resin that is capable of forming a coating film having extremely excellent curability, processability, retort resistance, content resistance, and dent resistance, and also provides a resin composition for a coating composition containing the polyester resin. The polyester resin obtained from a polycarboxylic acid component and a polyol component, wherein the polyester resin meets the conditions (i) to iii) described below: (i) among the polycarboxylic acid components constituting the polyester resin, the total copolymerization ratio of terephthalic acid component and 2,6-naphthalenedicarboxylic acid component is 80 mol % or more; (ii) among the polycarboxylic acid components constituting the polyester resin, the copolymerization ratio of 2,6-naphthalenedicarboxylic acid component is 2 to 80 mol %; and (iii) among the polyol components constituting the polyester resin, the total copolymerization ratio of ethylene glycol component and 1,2-propylene-glycol component is 50 mol % or more, wherein the copolymerization ratio of 1,2-propylene-glycol component is excessive relative to the copolymerization ratio of the ethylene glycol component.
1. A resin composition for can coating comprising a polyester resin, a blocked isocyanate compound and a curing catalyst,
wherein the composition comprises at least 65% by weight of the polyester resin relative to the total weight of the composition,
wherein a weight ratio of the polyester resin to the blocked isocyanate compound (polyester resin/blocked isocyanate compound) is 90/10 to 75/25,
wherein the polyester resin is obtained from a polycarboxylic acid component and a polyol component, wherein the polyester resin meets the conditions (i) to (vii) described below:
(i) among the polycarboxylic acid components constituting the polyester resin, the total copolymerization ratio of terephthalic acid component and 2,6-naphthalenedicarboxylic acid component is 95 to 100 mol %;
(ii) among the polycarboxylic acid components constituting the polyester resin, the copolymerization ratio of 2,6-naphthalenedicarboxylic acid component is 4 to 18 mol %;
(iii) among the polyol components constituting the polyester resin, the total copolymerization ratio of ethylene glycol component and 1,2-propylene-glycol component is 80 to 100 mol %;
(iv) among the polyol components constituting the polyester resin, the copolymerization ratio of 1,2-propylene-glycol component is excessive relative to the copolymerization ratio of the ethylene glycol component;
(v) among the polyol components constituting the polyester resin, the copolymerization ratio of ethylene glycol component is 10 to 30 mol %;
(vi) among the polyol components and the polycarboxylic acid components constituting the polyester resin, the total copolymerization ratio of a tri- or higher functional polyol and a tri- or higher functional polycarboxylic acid is 0.5 to 1 mol %; and
(vii) wherein the polyester resin has a glass transition temperature (Tg) of 72° C. or more, and an acid value of 85 eq/t or less.
2. A method for producing a coated metal plate for can comprising a step of applying the resin composition for can coating of claim 1 to a metal plate and curing the resin composition.
3. A coated metal plate for forming a can wherein on a surface of said metal plate a layer comprising a cured product of the resin composition according to claim 1 is placed.
4. A can comprising the coated metal plate of claim 3 .
5. The resin composition for can coating according to claim 1 , wherein the polyester resin has a reduced viscosity of 0.3 to 0.7 dl/g, and a specific gravity (30° C.) of 1.245 or more.
6. A coated metal plate for can on which a layer comprising a cured product of the resin composition for can coating according to claim 5 is placed on the surface of the metal plate.