Polyethylene microporous membrane and process for manufacturing same

1. A polyethylene microporous membrane having a Gurley air permeability of 1 to 1,000 sec/100 mL/25 μm and a total length of waviness widths in a width direction of the polyethylene microporous membrane is not more than one-third of an overall width of the microporous membrane, wherein the waviness widths are defined as portions of the microporous membrane, when the microporous membrane is placed on a flat surface, that are elevated off of the surface and lengths of waviness widths are lengths of those elevated portions measured relative to the width of the microporous membrane.

2. The polyethylene microporous membrane according to claim 1 , wherein a load necessary to remove slack is 0 to 300 g/mm 2 .

3. The polyethylene microporous membrane according to claim 2 , having a porosity of 15 to 85%.

4. The polyethylene microporous membrane according to claim 1 , having a porosity of 15 to 85%.

5. A composite membrane obtained by providing a coating layer on at least one surface of the polyethylene microporous membrane according to claim 1 .

6. A battery comprising as a separator the polyethylene microporous membrane according to claim 1 .

7. A composite membrane obtained by providing a coating layer on at least one surface of the polyethylene microporous membrane according to claim 2 .

8. A composite membrane obtained by providing a coating layer on at least one surface of the polyethylene microporous membrane according to claim 4 .

9. A battery comprising as a separator the composite membrane according to claim 5 .

10. A process of producing the polyethylene microporous membrane according to claim 1 , comprising:

(a) preparing a polyethylene solution by heat-dissolving polyethylene or a polyethylene composition in a solvent;

(b) extruding the solution of polyethylene or polyethylene composition through a die to form an extrudate;

(c) cooling the extrudate to form a gel-like sheet;

(d) stretching the gel-like sheet;

(e) removing the solvent from the stretched gel-like sheet to obtain a microporous membrane;

(f) stretching the microporous membrane from which the solvent has been removed; and

(g) following (f), heat-relaxing the microporous membrane at least in the longitudinal direction at a temperature equal to or higher than 50° C., wherein the heat-relaxing is performed by utilizing a difference in peripheral speed between rolls.

11. The process according to claim 10 , wherein a relaxation rate in the heat-relaxing is more than 0% but not more than 30% in the longitudinal direction.

12. A process of producing the polyethylene microporous membrane according to claim 2 , comprising:

(a) preparing a polyethylene solution by heat-dissolving polyethylene or a polyethylene composition in a solvent;

(b) extruding the solution of polyethylene or polyethylene composition through a die to form an extrudate;

(c) cooling the extrudate to form a gel-like sheet;

(d) stretching the gel-like sheet;

(e) removing the solvent from the stretched gel-like sheet to obtain a microporous membrane;

(f) stretching the microporous membrane from which the solvent has been removed; and

(g) following (f), heat-relaxing the microporous membrane at least in the longitudinal direction at a temperature equal to or higher than 50° C.

13. A process of producing the polyethylene microporous membrane according to claim 4 , comprising:

(a) preparing a polyethylene solution by heat-dissolving polyethylene or a polyethylene composition in a solvent;

(b) extruding the solution of polyethylene or polyethylene composition through a die to form an extrudate;

(c) cooling the extrudate to form a gel-like sheet;

(d) stretching the gel-like sheet;

(e) removing the solvent from the stretched gel-like sheet to obtain a microporous membrane;

(f) stretching the microporous membrane from which the solvent has been removed; and

(g) following (f), heat-relaxing the microporous membrane at least in the longitudinal direction at a temperature equal to or higher than 50° C.

14. A process of producing the polyethylene microporous membrane according to claim 5 , comprising:

(a) preparing a polyethylene solution by heat-dissolving polyethylene or a polyethylene composition in a solvent;

(b) extruding the solution of polyethylene or polyethylene composition through a die to form an extrudate;

(c) cooling the extrudate to form a gel-like sheet;

(d) stretching the gel-like sheet;

(e) removing the solvent from the stretched gel-like sheet to obtain a microporous membrane;

(f) stretching the microporous membrane from which the solvent has been removed; and

(g) following (f), heat-relaxing the microporous membrane at least in the longitudinal direction at a temperature equal to or higher than 50° C.