METHOD OF IMPREGNATING CERAMIC CORES FOR THE MANUFACTURE OF TURBOMACHINE BLADES
Impregnation method for mechanically reinforcing a ceramic core used in the manufacture of turbomachinery components by the lost wax casting method, involving dipping the core into a mixture obtained by dissolving polyvinyl alcohol in water, followed by an immersing of the core in pure water and hot polymerization, characterized in that the dosage is between 100 and 200 g of PVAl per litre of water. The dipping impregnation time is preferably between 20 min and 1 h 30.
1 . A method of impregnation for mechanically reinforcing a ceramic core the method comprising:
dipping the core in a mixture comprising polyvinyl alcohol and water, and
subsequently immersing the core in pure water and polymerizing via hot polymerisation,
wherein:
the mixture comprises between 100 and 200 g of polyvinyl alcohol per litre of water.
2 . The method according to claim 1 , wherein said dipping lasts for a period of between 20 minutes and 1 hour 30 minutes.
3 . The method according to claim 1 , wherein the polymerisation takes place at a temperature of between 90° C. and 120° C.
4 . The method according to claim 3 , wherein the polymerisation takes place for a period of between 30 minutes and 2 hours.
5 . A method for manufacturing turbine engine blades with internal cavities, the method comprising:
producing a ceramic core representing the internal cavities,
wherein the core is mechanically reinforced via the method according to claim 1 .
6 . The method according to claim 1 , wherein the core is suitable for manufacturing turbine engine parts via lost-wax casting.
7 . The method according to claim 5 , wherein the turbine engine is manufactured by lost-wax casting.