Flexible medical article and method of making the same
View Patent ↗A method of making a flexible medical article or tube, for example, a sheath for a vascular access device, is provided. The method can include extruding a polymer, for example, a polycarbonate-urethane copolymer, to form a tube and annealing the extruded polymer. The method can further include cutting the extruded tube to a desired length before or after annealing, flaring one end of the annealed tube and over-molding the flared portion onto a hub, and forming the other end of the tube into a tip. A sheath formed by such a method is also provided.
1. A method for forming a flexible medical article, the method comprising the following steps:
forming a tubular member of a medical article by extruding a polycarbonate urethane copolymer;
annealing said extruded tubular member of the medical article to increase a flexibility of said tubular member of the medical article; and
coupling a hub to a first end of the annealed tubular member of the medical article.
2. The method of claim 1 , wherein annealing comprises annealing said tubular member of the medical article at about 120° C. for about one hour.
3. The method of claim 1 , wherein the polycarbonate urethane copolymer is selected to have the property of reduced rigidity when exposed to heat.
4. The method of claim 1 , further comprising cutting said tubular member of the medical article.
5. The method of claim 1 , further comprising flaring the first end of said tubular member of the medical article so that the first end is configured to be coupled to the hub.
6. The method of claim 1 , further comprising over-molding the first end of the tubular member of the medical article onto the hub.
7. The method of claim 1 , further comprising forming a second end of the tubular member of the medical article into a tip.
8. The method of claim 1 , wherein the tubular member is annealed sufficiently so as to be capable of bending at an angle up to about 120° without kinking.
9. The method of claim 1 , wherein the tubular member is capable of withstanding pressures up to 300 psi.
10. The method of claim 1 , wherein the tubular member is capable of withstanding flow rates of up to 130 ml/min.
11. The method of claim 1 wherein the medical article further comprises:
a needle having a needle shaft and a needle hub;
a dilator having a dilator shaft and a dilator hub; and
a guidewire,
wherein the dilator shaft is coaxially disposed on the needle shaft with the needle hub and dilator hub juxtaposed, the guidewire is at least partially disposed in the needle, and the tubular member is coaxially disposed on the dilator shaft with the hub juxtaposed the dilator hub.
12. The method of claim 11 wherein the medical article further comprises a track along which the needle hub travels, the track being attached to the dilator hub.
13. The method of claim 1 , further comprising a step of cutting said extruded tubular member of the medical article into a desired length after the step of forming a tubular member of a medical article by extruding a polycarbonate urethane copolymer.
14. The method of claim 13 , further comprising a step of forming a second end of the tubular member into a tip after the step of annealing said extruded tubular member of the medical article to increase a flexibility of said tubular member of the medical article.
15. The method of claim 13 , wherein annealing comprises annealing said tubular member of the medical article at about 120° C. for about one hour.
16. The method of claim 14 , wherein annealing comprises annealing said tubular member of the medical article at about 120° C. for about one hour.
17. The method of claim 13 , wherein the method further comprises flaring the first end of the tubular member of the medical article to be coupled to the hub and over-molding the flared end onto the hub.
18. The method of claim 14 , wherein the method further comprises flaring the first end of the tubular member of the medical article to be coupled to the hub and over-molding the flared end onto the hub.
19. The method of claim 13 , wherein the polycarbonate urethane copolymer is selected to have the property of reduced rigidity when exposed to heat.
20. The method of claim 14 , wherein the polycarbonate urethane copolymer is selected to have the property of reduced rigidity when exposed to heat.