Unoriented film based on soft polypropylene

1. Unoriented film comprising at least one layer (L1), said layer (L1) comprises at least 70 wt. % of a polymer composition (Co), said composition (Co) comprises:

(a) a propylene copolymer (A) having

(a1) a melt flow rate MFR 2 (230° C.) measured according to ISO 1133 in the range of more than 2.0 to 15.0 g/10 min,

(a2) a comonomer content in the range of more than 7.5 to 16.5 wt. %,

(a3) a xylene cold soluble content (XCS) determined according ISO 16152 (25° C.) in the range of 20.0 to 55.0 wt. %, and

(a4) a melting temperature in the range of 146 to 151° C.,

wherein

(a5) the comonomer content of xylene cold soluble (XCS) fraction of the propylene copolymer is in the range of 14.0 to 30.0 wt. %, and

(b) a styrenic based elastomer(s) (B) having a styrene content in the range of 5 to equal or below 15 wt. %.

2. Unoriented film according to claim 1 , wherein the unoriented film is a mono-layer or at least a three layer film comprising the layers (L1), (L2) and (L3) with the stacking order (L2)/(L1)/(L3).

3. Unoriented film according to claim 1 , wherein the weight ratio of propylene copolymer (A) and the styrenic based elastomer(s) (B) [(A)/(B)] in the composition (Co) is in the range of 9/1 to 3/2.

4. Unoriented film according to claim 1 , wherein the propylene copolymer (A)

(a) has a melt flow rate MFR 2 (230° C.) measured according to ISO 1133 in the range of more than 2.5 to below 5.0 g/10 min, and/or

(b) fulfills inequation (I):

0.3

≤

Co

⁢

⁢

(

total

)

Co

⁢

⁢

(

XCS

)

≤

0.7

(

I

)

wherein, Co (total) is the comonomer content [wt. %] of the propylene copolymer (A),

Co (XCS) is the content of the xylene cold soluble fraction (XCS) [wt. %] of the propylene copolymer (A), and/or

(c) fulfills inequation (II):

Co

⁢

⁢

(

total

)

XCS

≤

0.30

(

II

)

wherein, Co (total) is the comonomer content [wt.-%] of the propylene copolymer (A), and

XCS is the content of the xylene cold soluble fraction (XCS) [wt. %] of the propylene copolymer (A).

5. Unoriented film according to claim 1 , wherein the xylene cold insoluble (XCI) fraction of the propylene copolymer (A) has a comonomer content in the range of 1.5 to 6.0 wt. %.

6. Unoriented film according to claim 1 , wherein the propylene copolymer (A) has an intrinsic viscosity (IV) of the xylene cold soluble (XCS) fraction in the range of equal or more than 1.5 to equal or below 3.0 dl/g, wherein the intrinsic viscosity (IV) is determined according to DIN ISO 1628/1.

7. Unoriented film according to claim 1 , wherein the styrenic based elastomer(s) (B) is(are) (a) styrene-ethylene/butylene-styrene (SEBS) block copolymer(s) (B-1) and/or (a) hydrogenated styrene-vinyl isoprene (SIS) block rubber(s) (B-2).

8. Unoriented film according to claim 1 , wherein the polymer composition (Co) comprises as styrenic based elastomer(s) (B) only (a) styrene-ethylene/butylene-styrene (SEBS) block copolymer(s) (B-1) and/or (a) hydrogenated styrene-vinyl isoprene (SIS) block rubber(s) (B-2).

9. Unoriented film according to claim 1 , wherein the styrenic based elastomer (B) has:

(a) a melt flow rate MFR 2 (230° C.) of below 10.0 g/10 min, and/or

(b) a density of below 0.905 g/m 3 .

10. Unoriented film according to claim 1 , wherein the propylene copolymer (A) is a heterophasic propylene copolymer (RAHECO) comprising a matrix (M) and an elastomeric propylene copolymer (E) dispersed in said matrix (M), wherein said matrix (M) is a random propylene copolymer (R-PP).

11. Unoriented film according to claim 10 , wherein;

(a) the weight ratio between the matrix (M) and the elastomeric propylene copolymer (E) is 50/50 to 90/10, and/or

(b) the comonomer content of the random propylene copolymer (R-PP) is in the range of 3.0 to 12.5 wt. %, and/or

(c) the random propylene copolymer (R-PP) has a xylene cold soluble (XCS) fraction in the range of 5.0 to 50.0 wt. %.

12. Unoriented film according to claim 1 , wherein the unoriented film is a cast film or a blown film.

13. Unoriented film according to claim 12 , wherein the cast film or blown film is rapidly cooled by water or sleeve touch technology.

14. A container, comprising the unoriented film according to claim 1 .

15. The container according to claim 14 , wherein the container or the film has been subjected to a sterilisation treatment.