Process for obtaining carbon black powder with reduced sulfur content
The present disclosure relates to a process for obtaining carbon black powder with a sulfur content of less than 0.07%. The process includes step of reacting carbon black powder with a sulfur content of 1-2% with an alkali metal or salt thereof, in a fluid media, at a temperature in the range of 100° C. to 350° C. and pressure in the range of 10 to 500 psig. It is found that in accordance with the process of the present disclosure, the sulfur content was reduced substantially from that of about 1.25% to that of 0.05%, resulting in about 96% desulfurization.
1. A process for obtaining carbon black powder with a sulfur content of less than 0.07%, the process comprising:
reacting, at a predetermined temperature and pressure, a carbon black powder having a sulfur content in the range of 1-2% with an alkali metal or salt thereof, in a fluid media, to form a reacted mixture containing an alkali sulfide derivative and a carbon black powder with a sulfur content of less than 0.07%; and
isolating the alkali sulfide derivative from the mixture to obtain the carbon black powder with a sulfur content of less than 0.07%.
2. The process of claim 1 , wherein the alkali metal or salt thereof is dispersed in the fluid media, prior to reacting with the carbon black powder.
3. The process of claim 1 , wherein the reaction is carried out under continuous stirring.
4. The process of claim 1 , wherein the alkali metal or salt thereof is a sodium metal.
5. The process of claim 1 , wherein the alkali metal or salt thereof is sodium hydroxide.
6. The process of claim 1 , wherein the fluid media comprises at least one compound selected from the group consisting of toluene, xylene, hexane, heptane, petrol, kerosene, crude oil, residual oil, ammonia, hydrogen gas, and nitrogen gas.
7. The process of claim 1 , wherein the fluid media comprises xylene.
8. The process of claim 1 , wherein the pre-determined pressure is in the range of 10 psig to 500 psig.
9. The process of claim 1 , wherein the pre-determined pressure is in the range of 14 psig to 50 psig.
10. The process of claim 1 , wherein the pre-determined temperature is in the range of 50° C. to 500° C.
11. The process of claim 1 , wherein the pre-determined temperature is in the range of 250° C. to 350° C.
12. The process of claim 1 , wherein the alkali sulfide derivative is isolated from the mixture by treating the mixture with water at a temperature in the range of 30° C. to 100° C.