Steel wire rod or steel bar having excellent cold forgeability
View Patent ↗A steel wire rod or steel bar as hot-rolled, including: by mass %: C: 0.1 to 0.6%, Si: 0.01 to 1.5%, Mn: 0.05 to 2.5%, Al: 0.015 to 0.3%, and N: 0.0040 to 0.0150%, and P: limited to 0.035% or less and S: limited to 0.025% or less, and the balance substantially consisting of iron and unavoidable impurities, wherein a depth of d (mm) from the surface of the surface layer region with 20 HV 0.2 or more higher, relative to HV 0.2 that is the average hardness in the region where the depth from the surface is from sectional radius R×0.5 (mm) to the center satisfies the formula (1); the steel structure of the surface layer region has a ferrite fraction of 10% or less by area ratio, with the balance being one or two or more of martensite, bainite and pearlite; the steel structure where the depth from the surface is from the sectional radius R×0.5 (mm) to the center is ferrite-pearlite or ferrite-bainite; and the surface roughness Ra in the circumferential direction when scales adhering to the surface have been removed is 4 μm or less.
1. A steel wire rod or steel bar as hot-rolled, having excellent cold forgeability, comprising:
by mass %, as a chemical composition,
C: 0.1 to 0.6%,
Si: 0.7% to 1.5%,
Mn: 0.05 to 2.5%,
Al: 0.015 to 0.3%,
N: 0.0040 to 0.0150%,
P: limited to 0.035% or less, and
S: limited to 0.025% or less, and a balance consisting of iron and unavoidable impurities, wherein a depth of d (mm) from a surface of a surface layer region with 20 HV 0.2 or more higher, relative to HV 0.2 that is an average hardness in a region where a depth from the surface is from sectional radius R×0.5 (mm) to a center satisfies the following formula (1); a steel structure of the surface layer region has a ferrite fraction of 10% or less by area ratio, with a balance being one or two or more of martensite, bainite and pearlite; the steel structure where the depth from the surface is from the sectional radius R×0.5 (mm) to the center is ferrite-pearlite or ferrite-bainite; and a surface roughness Ra in the circumferential direction when scales adhering to the surface have been removed is 4 μm or less,
0.5 ≧d/R ≧0.03 (1).
2. The steel wire rod or steel bar according to claim 1 , further comprising one or two or more of,
by mass %, as the chemical composition of the steel,
Cr: 3.0% or less,
Mo: 1.5% or less,
Cu: 2.0% or less,
Ni: 5.0% or less, and
B: 0.0035% or less.
3. The steel wire rod or steel bar according to claim 1 , further comprising one or two or more of,
by mass %, as the chemical composition of the steel,
Ca: 0.005% or less,
Zr: 0.005% or less,
Mg: 0.005% or less, and
Rem: 0.015% or less.
4. The steel wire rod or steel bar according to any of claim 1 , further comprising one or two or more of,
by mass %, as the chemical composition of the steel,
Ti: 0.20% or less,
Nb: 0.1% or less,
V: 1.0% or less, and
W: 1.0% or less.
5. The steel wire rod or steel bar according to any of claim 1 , further comprising one or two or more of,
by mass %, as a chemical composition of the steel,
Sb: 0.0150% or less,
Sn: 2.0% or less,
Zn: 0.5% or less,
Te: 0.2% or less,
Bi: 0.5% or less, and
Pb: 0.5% or less.
6. The steel wire rod or steel bar according to any of claim 1 , further satisfying the following formula (2), by mass %, as the chemical composition of the steel,
31Si+15Mn+23Cr+26Mo+100V≧55 Formula (2).
7. The steel wire rod or steel bar according to any of claim 1 , further comprising:
by mass %, as the chemical composition of the steel,
Ti: 0.02 to 0.20% and
B: 0.0005 to 0.0035%.
8. The steel wire rod or steel bar according to claim 2 , further comprising one or two or more of,
by mass %, as the chemical composition of the steel,
Ca: 0.005% or less,
Zr: 0.005% or less,
Mg: 0.005% or less, and
Rem: 0.015% or less.
9. The steel wire rod or steel bar according to any of claim 2 , further comprising one or two or more of,
by mass %, as the chemical composition of the steel,
Ti: 0.20% or less,
Nb: 0.1% or less,
V: 1.0% or less, and
W: 1.0% or less.
10. The steel wire rod or steel bar according to any of claim 3 , further comprising one or two or more of,
by mass %, as the chemical composition of the steel,
Ti: 0.20% or less,
Nb: 0.1% or less,
V: 1.0% or less, and
W: 1.0% or less.
11. The steel wire rod or steel bar according to any of claim 2 , further comprising one or two or more of,
by mass %, as a chemical composition of the steel,
Sb: 0.0150% or less,
Sn: 2.0% or less,
Zn: 0.5% or less,
Te: 0.2% or less,
Bi: 0.5% or less, and
Pb: 0.5% or less.
12. The steel wire rod or steel bar according to any of claim 3 , further comprising one or two or more of,
by mass %, as a chemical composition of the steel,
Sb: 0.0150% or less,
Sn: 2.0% or less,
Zn: 0.5% or less,
Te: 0.2% or less,
Bi: 0.5% or less, and
Pb: 0.5% or less.
13. The steel wire rod or steel bar according to any of claim 4 , further comprising one or two or more of,
by mass %, as a chemical composition of the steel,
Sb: 0.0150% or less,
Sn: 2.0% or less,
Zn: 0.5% or less,
Te: 0.2% or less,
Bi: 0.5% or less, and
Pb: 0.5% or less.
14. The steel wire rod or steel bar according to any of claim 2 , further satisfying the following formula (2), by mass %, as the chemical composition of the steel,
31Si+15Mn+23Cr+26Mo+100V≧55 Formula (2).
15. The steel wire rod or steel bar according to any of claim 3 , further satisfying the following formula (2), by mass %, as the chemical composition of the steel,
31Si+15Mn+23Cr+26Mo+100V≧55 Formula (2).
16. The steel wire rod or steel bar according to any of claim 4 , further satisfying the following formula (2), by mass %, as the chemical composition of the steel,
31Si+15Mn+23Cr+26Mo+100V≧55 Formula (2).
17. The steel wire rod or steel bar according to any of claim 5 , further satisfying the following formula (2), by mass %, as the chemical composition of the steel,
31Si+15Mn+23Cr+26Mo+100V≧55 Formula (2).
18. The steel wire rod or steel bar according to any of claim 2 , further comprising:
by mass %, as the chemical composition of the steel,
Ti: 0.02 to 0.20% and
B: 0.0005 to 0.0035%.
19. The steel wire rod or steel bar according to any of claim 3 , further comprising:
by mass %, as the chemical composition of the steel,
Ti: 0.02 to 0.20% and
B: 0.0005 to 0.0035%.
20. The steel wire rod or steel bar according to any of claim 4 , further comprising:
by mass %, as the chemical composition of the steel,
Ti: 0.02 to 0.20% and
B: 0.0005 to 0.0035%.