Binders, electrolytes and separator films for energy storage and collection devices using discrete carbon nanotubes
View Patent ↗In various embodiments an improved binder composition, electrolyte composition and a separator film composition using discrete carbon nanotubes. Their methods of production and utility for energy storage and collection devices, like batteries, capacitors and photovoltaics, is described. The binder, electrolyte, or separator composition can further comprise polymers. The discrete carbon nanotubes further comprise at least a portion of the tubes being open ended and/or functionalized. The utility of the binder, electrolyte or separator film composition includes improved capacity, power or durability in energy storage and collection devices. The utility of the electrolyte and or separator film compositions includes improved ion transport in energy storage and collection devices.
1. An electrode paste for a lead-acid battery comprising:
a plurality of discrete, debundled, unentangled multi-wall oxidized carbon nanotubes having an average length from about 400 to about 1400 nm; and polyvinyl alcohol, wherein the nanotubes contain about 1.5-6% by weight of oxygenated species, wherein at least a portion of the discrete carbon nanotubes are open ended, wherein a portion of discrete carbon nanotubes that are open ended are ion conducting, wherein 40% to 90% by number of the discrete carbon nanotubes have an aspect ratio of 30-70, and wherein from 1% to 30% by number of carbon nanotubes have an average aspect ratio 80-140.
2. The electrode paste of claim 1 , wherein the electrode paste is an anode paste.
3. The electrode paste of claim 1 , further comprising water, lead oxide and sulfuric acid.
4. The electrode paste of claim 1 , wherein a battery comprising said paste shows a higher charge efficiency of at least 30% at 14.2 v charging voltage, relative to a control battery which comprises an electrode paste which does not comprise discrete carbon nanotubes.
5. The electrode paste of claim 1 , wherein a battery comprising said paste shows an increased rate of charge of at least 200%, relative to a control battery which comprises an electrode paste which does not comprise discrete carbon nanotubes.
6. The electrode paste of claim 1 , wherein a battery comprising said paste shows at least 50% lower polarization between 14 and 15 volts, relative to a control battery which comprises an electrode paste which does not comprise discrete carbon nanotubes.
7. An electrode paste for a lead-acid battery comprising:
a plurality of discrete, debundled, unentangled multi-wall oxidized carbon nanotubes having an average length from about 400 to about 1400 nm; wherein the nanotubes contain about 1.5-6% by weight of oxygenated species, wherein at least a portion of the discrete carbon nanotubes are open ended, and wherein a portion of discrete carbon nanotubes that are open ended are ion conducting, wherein 40% to 90% by number of the discrete carbon nanotubes have an aspect ratio of 30-70, and wherein from 1% to 30% by number of carbon nanotubes have an average aspect ratio 80-140.
8. The electrode paste of claim 7 , wherein a battery comprising said paste shows a higher charge efficiency of at least 30% at 14.2 v charging voltage, relative to a control battery which comprises an electrode paste which does not comprise discrete carbon nanotubes.
9. The electrode paste of claim 7 , wherein a battery comprising said paste shows an increased rate of charge of at least 200%, relative to a control battery which comprises an electrode paste which does not comprise discrete carbon nanotubes.
10. An electrode paste for a lead-acid battery comprising:
lead oxide, acid, water, and a plurality of discrete, debundled, unentangled multi-wall oxidized carbon nanotubes having an average length from about 400 to about 1400 nm; wherein the nanotubes contain about 1.5-6% by weight of oxygenated species, wherein at least a portion of the discrete carbon nanotubes are open ended, and wherein a portion of discrete carbon nanotubes that are open ended are ion conducting, wherein 40% to 90% by number of the discrete carbon nanotubes have an aspect ratio of 30-70, and wherein from 1% to 30% by number of carbon nanotubes have an average aspect ratio 80-140.
11. The electrode paste of claim 10 , wherein a battery comprising said paste shows a higher charge efficiency of at least 30% at 14.2 v charging voltage, relative to a control battery which comprises an electrode paste which does not comprise discrete carbon nanotubes.
12. The electrode paste of claim 10 , wherein a battery comprising said paste shows an increased rate of charge of at least 200%, relative to a control battery which comprises an electrode paste which does not comprise discrete carbon nanotubes.