Energy storage system preventing self from overheating, a method for preventing energy storage system from overheating and a method for forming a heat dissipation coating on energy storage system
The present invention discloses an overheat prevention energy storage system preventing self from overheating, comprising a heat dissipating external surface, wherein at least a portion of the external surface is coated with at least one layer of heat dissipation coating of high emissivity. The present invention further discloses a method for preventing overheat of the energy storage system and a method for forming at least one layer of heat dissipation coating of high emissivity onto at least part of an external surface of the energy storage system or assemblies thereof.
1. An energy storage system, comprising energy storage units each having two externally exposed terminal posts, an electrical connection element between the energy storage units, and a heat dissipating external surface, wherein the heat dissipating external surface comprises at least a portion of the externally exposed surface of at least one terminal post and/or the electrical connection element and wherein the heat dissipating external surface is coated or formed with at least one layer of heat dissipation coating having a black body radiation rate of greater than 0.8 and a thermal conductivity of greater than 150 W/m·K at a temperature of 300K.
2. The energy storage system according to claim 1 , wherein the heat dissipation coating comprises nano particles.
3. The energy storage system according to claim 2 , wherein the nano particles comprise carbon nanotubes.
4. The energy storage system according to claim 2 , wherein the nano particles have a particle size of less than 100 nanometers.
5. The energy storage system according to claim 1 , wherein the heat dissipation coating is cured at a temperature ranging from 40-100° C.
6. The energy storage system according to claim 5 , wherein the heat dissipation coating is cured at a temperature of 50° C.
7. The energy storage system according to claim 1 , wherein each layer of the heat dissipation coating has a thickness of 200-300 μm.
8. The energy storage system according to claim 1 , wherein composition, thickness, or curing temperature and time for each layer of the heat dissipation coating is identical or different.
9. The energy storage system according to claim 7 , wherein the number of the layers of the heat dissipation coating is 2, 3 or 4.
10. The energy storage system according to claim 1 , wherein the energy storage system is a valve-regulated type lead-acid battery or a system thereof.
11. A method for preventing overheating of an energy storage system comprising energy storage units each having two externally exposed terminal posts, an electrical connection element between the energy storage units, and a heat dissipating surface comprising at least a portion of the externally exposed surface of at least one terminal post and/or the electrical connection element, the method comprising coating or forming the heat dissipating surface with at least one layer of heat dissipation coating having a black body radiation rate of greater than 0.8 and a thermal conductivity of greater than 150 W/m·K at a temperature of 300K.
12. A method for applying or forming at least one layer of heat dissipation coating onto an external surface of an energy storage system, comprising the following steps in sequence:
(1) mixing active ingredients or precursor of the coating and stirring until a uniform paint mixture is formed;
(2) applying the uniform paint mixture onto the external surface to form a homogeneous coating;
(3) curing the coating at a curing temperature equal to or above room temperature until it is cured completely; and
(4) optionally, repeating the above steps (1), (2) and (3) in sequence to form multiple layers of the heat dissipation coating onto the external surface;
wherein the energy storage system comprises energy storage units each having two externally exposed terminal posts, an electrical connection element between the energy storage units, and an external surface;
wherein at least a portion of the external surface to which the uniform paint mixture is applied comprises an externally exposed surface of at least one terminal post and/or the electrical connection element; and
wherein the heat dissipation coating has a black body radiation rate of greater than 0.8 and a thermal conductivity of greater than 150 W/m·K at a temperature of 300K.
13. The method according to claim 12 , wherein the heat dissipation coating comprises nano particles.
14. The method according to claim 13 , wherein the nano particles comprise carbon nanotubes.
15. The method according to claim 14 , wherein the heat dissipation coating has a curing temperature ranging from 40-100° C.
16. The method according to claim 15 , wherein the heat dissipation coating has a curing temperature of 50° C.
17. The method according to claim 12 , wherein the heat dissipation coating a thickness of 200-300 μm.
18. The method according to claim 12 , wherein paint composition, thickness, or curing temperature and time for each layer of the heat dissipation coating is identical or different.
19. The method according to claim 17 , wherein the number of the layers of the heat dissipation coating is 2, 3 or 4.