Method for producing plug for piercing-rolling
View Patent ↗Provided is a method for producing a plug for use in a piercing-rolling mill for producing a seamless steel tube/pipe, and the method for producing the plug for piercing-rolling comprises shotblasting a surface of the plug, and arc-spraying a spray wire so as to form a film on a surface of a base metal of the plug that is shotblasted. In the arc-spraying step, the arc spraying is carried out by using, as the spray wire, a cored wire whose iron sheath tube is charged with at least iron oxide particles among iron particles and the iron oxide particles (one or more of FeO particles, Fe 3 O 4 particles, and Fe 2 O 3 particles), so as to form the film containing iron oxide and Fe. Accordingly, it is possible to enhance the production efficiency of the plug, and to produce the plug for piercing-rolling capable of securing the steady enhancement of the durability life of the plug during the piercing-rolling.
1. A method for producing a plug for use in a piercing-rolling mill for producing a seamless steel tube/pipe, the method comprising:
shotblasting a surface of the plug; and
arc-spraying a spray wire so as to form a film on a surface of a base metal of the plug that is shotblasted, wherein
in the arc-spraying step, the arc-spraying is carried out by using, as the spray wire, a cored wire whose iron sheath tube is charged with at least iron oxide particles so as to form the film containing iron oxides and Fe,
wherein the iron sheath charged with at least iron oxide particles results in a reduction in a time required to form the film having a predetermined oxide proportion on the surface of the base metal of the plug.
2. The method for producing a plug for piercing-rolling according to claim 1 , wherein
the iron oxide particles comprise one or more of FeO particles, Fe 3 O 4 particles, and Fe 2 O 3 particles.
3. The method for producing a plug for piercing-rolling according to claim 1 , wherein the iron sheath tube is charged further with iron particles.