Case hardening steel material
View Patent ↗A case hardening steel material having a chemical composition consists of, by mass percent, C: 0.15 to 0.23%, Si: 0.01 to 0.15%, Mn: 0.65 to 0.90%, S: 0.010 to 0.030%, Cr: 1.65 to 1.80%, Al: 0.015 to 0.060%, and N: 0.0100 to 0.0250%, further containing, as necessary, one or more kinds selected from Cu and Ni of predetermined amounts, the balance being Fe and impurities; 25≦Mn/S≦85, 0.90≦Cr/(Si+2Mn)≦1.20, and 1.16Si+0.70Mn+Cr≧2.20; P, Ti and O in the impurities being P≦0.020%, Ti≦0.005%, and O≦0.0015%; and having a structure consisting of 20 to 70% in an area ratio being ferrite; and the portion other than the ferrite being one or more kinds of pearlite and bainite. The steel material is used suitably as a raw material of the carburized part such as a CVT pulley shaft.
1. A case hardening steel material having a chemical composition consisting of, by mass percent, C: 0.15 to 0.23%, Si: 0.01 to 0.15%, Mn: 0.65 to 0.90%, S: 0.023 to 0.030%, Cr: 1.65 to 1.80%, Al: 0.015 to 0.060%, and N: 0.0100 to 0.0250%, the balance being Fe and impurities;
Fn1, Fn2 and Fn3 represented by the following Formulas (1), (2), and (3) being 25≦Fn1≦85, 0.90≦Fn2≦1.20, and Fn3≦2.20, respectively; and
the contents of P, Ti and O in the impurities being P: 0.020% or less, Ti: 0.005% or less, and O: 0.0015% or less, and
having a structure consisting of 20 to 70% in an area ratio being ferrite; and
the portion other than the ferrite being one or more kinds of pearlite and bainite:
Fn1=Mn/S (1)
Fn2=Cr/Si+2Mn) (2)
Fn3=1.16Si+0.70Mn+Cr (3)
wherein, the element symbol in the Formulas (1), (2), and (3) represents the content by mass percent of the element.
2. A case hardening steel material having a chemical composition consisting of, by mass percent, C: 0.15 to 0.23%, Si: 0.01 to 0.15%, Mn: 0.65 to 0.90%, S: 0.023 to 0.030%, Cr: 1.65 to 1.80%, Al: 0.015 to 0.060%, N: 0.0100 to 0.0250%, and one or more kinds selected from Cu: 0.20% or less and Ni: 0.20% or less, the balance being Fe and impurities;
Fn1, Fn2 and Fn3 represented by the following Formulas (1), (2), and (3) being 25≦Fn1≦85, 0.90≦Fn2≦1.20, and Fn3≦2.20, respectively; and
the contents of P, Ti and O in the impurities being P: 0.020% or less, Ti: 0.005% or less, and O: 0.0015% or less, and
having a structure consisting of 20 to 70% in an area ratio being ferrite; and
the portion other than the ferrite being one or more kinds of pearlite and bainite:
Fn1=Mn/S (1)
Fn2=Cr/(Si+2Mn) (2)
Fn3=1.16Si+0.70Mn+Cr (3)
wherein, the element symbol in the Formulas (1), (2), and (3) represents the content by mass percent of the element.