Seamless steel pipe and method for producing the same
View Patent ↗There is provided a seamless steel pipe having high strength and high toughness even if having a thick wall. A seamless steel pipe according to the present embodiment consists of: in mass %, C: 0.03 to 0.08%, Si: not more than 0.25%, Mn: 0.3 to 2.0%, P: not more than 0.05%, S: not more than 0.005%, Al: 0.001 to 0.10%, Cr: 0.02 to 1.0%, Ni: 0.02 to 1.0%, Mo: 0.02 to 0.8%, N: 0.002 to 0.008%, Ca: 0.0005 to 0.005%, and Nb: 0.01 to 0.1%, the balance being Fe and impurities, and has a wall thickness of not less than 50 mm. In a cross section perpendicular to an axial direction of the seamless steel pipe, an average crystal grain size of prior austenite grains in a near surface portion is less than 80 μm, the near surface portion being a 500 μm×500 μm area centered at a position of a depth of 2 mm from a surface, and a difference between the average crystal grain size of the prior austenite grains in the near surface portion and an average crystal grain size of prior austenite grains in a central portion of a wall thickness of the cross section is less than 50 μm, the central portion being a 500 μm×500 μm area centered at a center position of the wall thickness.
1. A seamless steel pipe consisting of: in mass %,
C: 0.03 to 0.08%,
S: not more than 0.25%,
Mn: 0.3 to 2.0%,
P: not more than 0.05%,
S: not more than 0.005%,
Al: 0.001 to 0.10%,
Cr: 0.02 to 1.0%,
Ni: 0.02 to 1.0%,
Mo: 0.02 to 0.8%,
N: 0.002 to 0.008%,
Ca: 0.0005 to 0.005%,
Nb: 0.03 to 0.1%, and
optionally one or more selected from the group consisting of Ti: not more than 0.010%, Cu: not more than 1.0%, and V: not more than 0.1%, and
the balance being Fe and impurities, and
having a wall thickness not less than 50 mm,
wherein in a cross section perpendicular to an axial direction of the seamless steel pipe, an average crystal grain size of prior austenite grains in a near surface portion is less than 80 μm, the near surface portion being a 500 μm×500 μm area centered at a position of a depth of 2 mm from a surface, and
wherein a difference between the average crystal grain size of the prior austenite grains in the near surface portion and an average crystal grain size of prior austenite grains in a central portion of a wall thickness in the cross section is less than 50 μm, the central portion being a 500 μm×500 μm area centered at a center position of the wall thickness of the seamless steel pipe; and,
the seamless steel pipe has a yield strength of not less than 551 MPa.
2. The seamless steel pipe according to claim 1 , containing:
Ti: 0.001 to 0.010%.
3. The seamless steel pipe according to claim 1 , containing: at least one selected from a group consisting of:
Cu: 0.1 to 1.0%, and
V: 0.01 to 0.1%.
4. The seamless steel pipe according to claim 2 , containing: at least one selected from a group consisting of:
Cu: 0.1 to 1.0%, and
V: 0.01 to 0.1%.