Tire rubber composite and pneumatic tire
View Patent ↗A rubber composition for tires comprises: per 100 parts by weight of diene rubber containing from 5 to 50 wt. % of terminally modified S-SBR, from 2 to 50 parts by weight of an aromatic modified terpene resin having a softening point of 100° C. or higher. A total content of 60 to 130 parts by weight of two types of silica, that is silica X and silica Y. A functional group of the modified S-SBR has reactivity with a silanol group. A proportion of the silica relative to a total amount of a reinforcing filler containing the silica X, the silica Y, and an optionally compounded carbon black is 85 wt. % or greater. A nitrogen adsorption specific surface area of the silica X is 140 m 2 /g or greater; a nitrogen adsorption specific surface area of the silica Y is greater than 100 m 2 /g and less than 140 m 2 /g.
1. A rubber composition for tires comprising: per 100 parts by weight of diene rubber containing from 5 to 50 wt. % of solution polymerization-produced terminally modified styrene-butadiene rubber (first modified S-SBR) having a vinyl unit content of 25 wt. % or greater and a glass transition temperature of −50° C. or lower and from 25 to 95 wt. % of solution polymerization-produced terminally modified styrene-butadiene rubber (second modified S-SBR) having a glass transition temperature of higher than −50° C., the total amount of the first modified S-SBR and the second modified S-SBR being 83 wt. % or greater,
from 2 to 50 parts by weight of an aromatic modified terpene resin having a softening point of 100° C. or higher,
a total content of 60 to 130 parts by weight of two types of silica, that is silica X and silica Y;
a functional group of the first modified S-SBR being a functional group having reactivity with a silanol group on a surface of the silica selected from the group consisting of a hydroxyl group-containing polyorganosiloxane structure, an alkoxysilyl group, a hydroxyl group, an aldehyde group, a carboxyl group, an amino group, an imino group, an epoxy group, an amide group, a thiol group, and an ether group;
a proportion of the silica relative to a total amount of a reinforcing filler containing the silica and a carbon black being 85 wt. % or greater;
a nitrogen adsorption specific surface area of the silica X being 140 m 2 /g or greater;
a nitrogen adsorption specific surface area of the silica Y being greater than 100 m 2 /g and less than 140 m 2 /g; and
if a compounded amount of the silica X relative to 100 parts by weight of the diene rubber is x parts by weight and a compounded amount of the silica Y relative to 100 parts by weight of the diene rubber is y parts by weight, a relationship x/7<y≦x being satisfied.
2. The rubber composition for tires according to claim 1 , wherein the functional group of the first modified S-SBR is a hydroxyl group.
3. The rubber composition for tires according to claim 1 , wherein the first modified S-SBR has the vinyl unit content of 50 wt. % or less.
4. The rubber composition for tires according to claim 1 , wherein the first modified S-SBR has the vinyl unit content of 25 to 30 wt. %.
5. The rubber composition for tires according to claim 1 , wherein the first modified S-SBR has the vinyl unit content of 30 to 43 wt. %.
6. The rubber composition for tires according to claim 1 , wherein the first modified S-SBR has the vinyl unit content of 43 to 50 wt. %.
7. The rubber composition for tires according to claim 1 , wherein the first modified S-SBR is solution polymerization-produced styrene-butadiene rubber in which a molecular terminal or both molecular terminals thereof are modified with functional group(s) having reactivity with a silanol group on the surface of the silica, the functional group being a hydroxyl group.
8. The rubber composition for tires according to claim 1 , wherein the content of the first modified S-SBR is from 10 to 30 wt. %.
9. The rubber composition for tires according to claim 1 , wherein the compounded amount of the aromatic modified terpene resin is from 10 to 15 parts by weight, relative to 100 parts by weight of the diene rubber.
10. The rubber composition for tires according to claim 1 , wherein the nitrogen adsorption specific surface area of the silica X comprises from about 150 m 2 /g to about 230 m 2 /g.
11. The rubber composition for tires according to claim 1 , wherein a nitrogen adsorption specific surface area of the silica Y is greater than 100 m 2 /g and 130 m 2 /g or less.
12. The rubber composition for tires according to claim 1 , wherein the total amount of the silica X and the silica Y (x+y) is from 80 to 130 parts by weight.
13. The rubber composition for tires according to claim 1 , wherein the proportion of silica is from 87 to 100 wt. %, relative to the total of 100 wt. % of the reinforcing filler that contains the silica.
14. The rubber composition for tires according to claim 1 , wherein the first modified S-SBR is contained from 5 to 17 wt. %.
15. The rubber composition for tires according to claim 14 , wherein the glass transition temperature of the first modified S-SBR is −63 to −50° C.
16. The rubber composition for tires according to claim 1 , wherein the nitrogen adsorption specific surface area of the silica X being 180 m 2 /g or greater.
17. A pneumatic tire using the rubber composition for tires described in claim 1 .
18. A pneumatic tire using the rubber composition for tires described in claim 2 .