Process for applying a protective layer to a turbine component
View Patent ↗A turbine component is provided, on which a protective layer is arranged, for example to avoid droplet impact erosion, wherein, in a first method step, a nanofilm is applied and a brazing metal is applied to the nanofilm, and the nanofilm chosen is one which, after initial ignition, leads to an exothermic reaction, whereby fusion of the brazing metal with the base material takes place to form a protective layer.
1. A process for producing a protective layer on a base material, comprising:
arranging a nanofilm directly on the base material and a brazing metal on the nanofilm,
forming the protective layer comprising the brazing metal by locally igniting the nanofilm to start an exothermic reaction in the nanofilm that heats and fuses the brazing metal onto the base material,
wherein the nanofilm forms nanofilm hard materials during the exothermic reaction, the method further comprising:
arranging the nanofilm and the brazing metal in such a manner that nanofilm hard materials which remain after the exothermic reaction are arranged in the manner of roof tiles or in the manner of fish scales, and
arranging a plurality of nanofilms with a plurality of brazing metals one on to of another before the exothermic reaction.
2. The process as claimed in claim 1 , further comprising:
arranging an additional protective layer on the brazing metal before locally igniting the nanofilm, and
bonding the additional protective layer to the protective layer via the exothermic reaction.
3. The process as claimed in claim 2 ,
wherein the additional protective layer comprises a ceramic material.
4. The process as claimed in claim 1 ,
wherein the nanofilm comprises: Al/Ni.
5. The process as claimed in claim 1 ,
wherein the braze metal comprises: Ag 59 Cu 27.5 In 12.5 Ti; TiCu 15 Ni 15 or TiZr 37.5 Cu 15 Ni 10 .
6. The process as claimed in claim 1 , wherein a turbine component of a gas turbine engine comprises the base material.
7. The process as claimed in claim 6 , wherein the protective layer defines an external layer of the turbine component.