ADHESIVE COMPOSITION CONTAINING UV CURABLE RUBBER, AND PROTECTIVE FILM USING SAME
The present invention provides an adhesive composition for a protective film, comprising a UV curable rubber having a degree of unsaturation of 70-85%. In addition, the present invention provides a protective film formed with the adhesive composition for a protective film.
1 . An adhesive composition for protective films, comprising:
a UV curable rubber having a degree of unsaturation from 70% to 85%.
2 . The adhesive composition according to claim 1 , wherein the UV curable rubber comprises at least one selected from the group consisting of isoprene, styrene, polybutadiene, acrylonitrile butadiene, butyl, polychloroprene, urethane, and acrylic rubbers.
3 . The adhesive composition according to claim 2 , wherein the styrene rubber comprises at least one selected from the group consisting of styrene-isoprene-styrene block copolymers, styrene-butadiene-styrene block copolymers, styrene-butylene-styrene block copolymers, styrene-propylene-styrene block copolymers, acrylonitrile-butylene-styrene copolymers, and carboxylic acid derivatives thereof.
4 . The adhesive composition according to claim 2 , wherein the styrene rubber comprises styrene in an amount of 15% to 30%.
5 . The adhesive composition according to claim 1 , wherein the UV curable rubber has a weight average molecular weight from 30,000 to 60,000.
6 . The adhesive composition according to claim 1 , wherein the UV curable rubber has a glass transition temperature from −60° C. to −40° C.
7 . The adhesive composition according to claim 1 , wherein the UV curable rubber has a surface energy from 30 mN/m to 40 mN/m.
8 . The adhesive composition according to claim 1 , further comprising:
0.1 parts by weight to 1 part by weight of a photopolymerization initiator based on 100 parts by weight of the UV curable rubber.
9 . A protective film formed of the adhesive composition according to claim 1 .
10 . The protective film according to claim 9 , wherein a substrate, onto which the adhesive composition is coated, comprises at least one selected from the group consisting of ester polymer films comprising polyethylene terephthalate, styrene polymer films comprising polystyrene, olefin polymer films comprising cycloolefin polymers, carbonate polymer films comprising polycarbonate, imide polymer films comprising polyimide, sulfone polymer films comprising polyethersulfone, cellulose polymer films comprising triacetyl cellulose, and acrylic polymer films comprising polymethyl methacrylate.