IP Library Granted Patent US 10,252,947
Granted Patent B2
US 10,252,947 · App. 14/404,034 · Granted Apr 9, 2019

Method of making a cBN material

Inventors: Gerold Weinl (Alvsjo, SE); Annika Kauppi (Hasselby, SE); Malin Martensson (Nacka, SE); Torbjorn Selinder (Bandhagen, SE); Rui Shao (Dublin, OH)
Assignee: HYPERION MATERIALS & TECHNOLOGIES (SWEDEN) AB
C04B35/645B22F3/10B22F3/14B22F9/04C04B35/583C04B35/5831C04B35/6261C04B35/62655C04B35/634C04B35/638C22C26/00C22C32/0047B22F9/026B22F2005/001B22F2009/041B22F2998/10C04B2235/386C04B2235/3843C04B2235/3847C04B2235/3852C04B2235/3856C04B2235/3882C04B2235/402C04B2235/404C04B2235/405C04B2235/5436C04B2235/6562C04B2235/6582C04B2235/661C04B2235/80
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 10,252,947
App. No.
14/404,034
Granted
Apr 9, 2019
Kind
B2
Abstract

A cBN material and a method of making a cBN material, the method including the steps of providing a powder mixture comprising cBN grains, aluminum and a Ti(CxNyOz)a powder, subjecting the powder mixture to a milling to form a powder blend, subjecting the powder blend to a forming operation to form a green body, subjecting the green body to a pre-sintering step, at a temperature between 650 to 950° C., to form a pre-sintered body, and subjecting the pre-sintered body to a HPHT operation to form the cBN material. For the Ti(CxNyOz)a powder, 0.05≤z≤0.4. In addition, a cBN material includes cBN grains, an Al2O3 phase, a binder phase of TiC, TiN and/or TiCN, W and Co, whereby a quotient Q is <0.25 of the cBN material.

Claims (36)

1. A method of making a cBN material comprising:

providing a powder mixture comprising cBN grains, aluminum and a Ti(C x N y O z ) a powder;

subjecting the powder mixture to a milling operation to form a powder blend;

subjecting the powder blend to a forming operation to form a green body;

subjecting said green body to a pre-sintering step, at a temperature between about 650 to about 950° C., to form a pre-sintered body; and

subjecting said pre-sintered body to a HPHT operation to form the cBN material, wherein for said Ti(C x N y O z ) a powder, 0.9≤a≤1.1; 0.5≤x≤0.95; 0≤y≤0.3; and 0.05≤z≤0.4.

2. A method according to claim 1 , wherein the Ti(C x N y O z ) a powder is provided in an amount of 10 to 70 wt % of the total dry powder weight of the powder mixture.

3. A method according to claim 1 , wherein for the Ti(C x N y O z ) a powder, 0.5≤x≤0.95, 0.0≤y≤0.3; and 0.1≤z≤0.3.

4. A method according to claim 1 , wherein 0.7≤x≤0.95 and stoichiometric TiN is added in an amount so that TiN replaces the Ti(C x N y O z ) a powder by between 5 to 55 wt %.

5. A method according to claim 4 , wherein 0.7≤x≤0.95 and stoichiometric TiN is added in an amount so that TiN replaces the Ti(C x N y O z ) a powder by between 25 to 55 wt %.

6. A method according to claim 1 , wherein the aluminum in the powder mixture is elemental aluminum.

7. A method according to claim 1 , wherein aluminum is provided in an amount of 1 to 10 wt % of the total dry powder weight of the powder mixture.

8. A method according to claim 1 , wherein W is added such that the amount of W is 1 to 12 wt % of the cBN material, and Co is added such that the amount of Co is between 0.5 to 9 wt % of the cBN material, where the W/Co ratio is between 1.0 to 2.0.

9. A method according to claim 1 , wherein a part of the Ti(C x N y O z ) a powder is replaced by stoichiometric TiN, TiC and/or TiCN.

10. A method according to claim 1 , wherein a milling liquid is added to the powder mixture to form a slurry and wherein the milling operation is followed by a drying operation to form the powder blend.

11. A method according to claim 10 , wherein the drying operation is done by spray drying.

12. A method according to claim 1 , wherein the pre-sintering is done at a temperature of between about 850° C. to about 930° C.

13. A method according to claim 1 , wherein the HPHT operation is performed at a pressure of about 55 to about 75 kbar and a temperature from about 1300 to about 1600° C.

14. A method of making a cBN material comprising:

providing a powder mixture comprising cBN grains, elemental aluminum and a Ti(C x N y O z ) a powder;

subjecting the powder mixture to a milling operation to form a powder blend;

subjecting the powder blend to a forming operation to form a green body;

subjecting said green body to a pre-sintering step, at a temperature between about 650 to about 950° C., to form a pre-sintered body; and

subjecting said pre-sintered body to a HPHT operation to form the cBN material,

wherein for said Ti(C x N y O z ) a powder, 0.9≤a≤1.1, 0.5≤x≤0.95; 0.00≤y≤0.3; and 0.1≤z≤0.3.

15. A method according to claim 14 , wherein 0.7≤x≤0.95 and stoichiometric TiN is added in an amount so that TiN replaces the Ti(C x N y O z ) a powder by between 5 to 55 wt %.

16. A method according to claim 15 , wherein 0.7≤x≤0.95 and stoichiometric TiN is added in an amount so that TiN replaces the Ti(C x N y O z ) a powder by between 25 to 55 wt %.

17. A method of making a cBN material comprising:

providing a powder mixture comprising cBN grains, elemental aluminum and a Ti(C x N y O z ) a powder;

subjecting the powder mixture to a milling operation to form a powder blend;

subjecting the powder blend to a forming operation to form a green body;

subjecting said green body to a pre-sintering step, at a temperature between about 650 to about 950° C., to form a pre-sintered body; and

subjecting said pre-sintered body to a HPHT operation to form the cBN material,

wherein for said Ti(C x N y O z ) a powder, 0.9≤a≤1.1, 0.3≤x≤0.95; 0.00≤y≤0.5; and 0.05≤z≤0.3.

18. A method according to claim 17 , wherein 0.7≤x≤0.95 and stoichiometric TiN is added in an amount so that TiN replaces the Ti(C x N y O z ) a powder by between 5 to 55 wt %.

19. A method according to claim 18 , wherein 0.7≤x≤0.95 and stoichiometric TiN is added in an amount so that TiN replaces the Ti(C x N y O z ) a powder by between 25 to 55 wt %.

Assignments (4)
ASSIGNEE'S CHANGE OF ADDRESS Recorded Aug 29, 2023
From: HYPERION MATERIALS & TECHNOLOGIES (SWEDEN) AB
To: HYPERION MATERIALS & TECHNOLOGIES (SWEDEN) AB
Reel/Frame 064828/0128 →
CHANGE OF NAME Recorded Jan 17, 2019
From: SANDVIK HYPERION AB
To: HYPERION MATERIALS & TECHNOLOGIES (SWEDEN) AB
Reel/Frame 048085/0327 →
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Aug 10, 2018
From: SANDVIK INTELLECTUAL PROPERTY AKTIEBOLAG
To: SANDVIK HYPERION AB
Reel/Frame 046762/0435 →
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Dec 3, 2014
From: MARTENSSON, MALIN; SELINDER, TORBJORN; KAUPPI, ANNIKA; WEINL, GEROLD; SHAO, RUI
To: SANDVIK INTELLECTUAL PROPERTY AB
Reel/Frame 034357/0525 →
Continuity (2)
Provisional Application 61653686 · May 31, 2012
Related Publication 20150110663A1 · Apr 23, 2015