Method for producing insulated electric wire

1. A method for producing an insulated electric wire, the method comprising:

a first step of processing a copper alloy containing a tin and inevitable impurities into a fine wire having a diameter of 0.21 mm±0.008 mm, the tin being 0.30 wt % or more and 0.39 wt % or less;

a second step of annealing the fine wire obtained in the first step so as to refine the fine wire to have an extension coefficient of 10% or more and 25% or less and a tensile strength of 300 MPa or more and 400 MPa or less; and

a third step of twisting seven fine wires having undergone the second step with a twist pitch of 15 mm±6 mm,

wherein when an annealing temperature of the second step is set as 400° C., an annealing time of the second step is between 300 seconds and 600 seconds,

wherein when the annealing temperature of the second step is set as 450° C., the annealing time of the second step is between 60 seconds and 600 seconds, and

wherein when the annealing temperature of the second step is set as 500° C., the annealing time of the second step is between 30 seconds and 180 seconds.

2. The method according to claim 1 , further comprising:

a fourth step of making a twisted wire obtained through the third step insulation-coated with a polyvinyl chloride resin composition having a smoking temperature of 170 degrees with a thickness of 0.27 mm or more and 0.35 mm or less, making the insulated electric wire to have a finishing outer diameter of 1.2 mm.