“No-bake” foundry mix with extended work time
View Patent ↗A “no-bake” process allows the forming of larger metal castings, by providing longer work times, in the range of about 45 to about 60 minutes. This is achieved using a liquid curing catalyst that is a pyridine, substituted at the second or third position with a moiety having a molecular weight in the range of about 30 to about 100 mwu. Examples of the liquid curing catalyst include 2-ethanolpyridine, 3-chloropyridine and 2-methoxypyridine. When combined with a two-part polyurethane binder precursor and a foundry aggregate, the liquid curing catalyst provides not only the longer work time, but also a strip time that is less than about 167% of the work time, as measured from the point of activating the polyurethane precursors by mixing them in the presence of the curing catalyst.
1. A binder composition for a foundry mix, comprising:
a polyurethane binder precursor, provided in two parts, the first part comprising a polyol component and the second part comprising a polyisocyanate component; and
a liquid curing catalyst that is 2-ethanolpyridine, the liquid curing catalyst being present in the range of about 5 to 7 weight percent based on the weight of the first part of the polyurethane binder component, selected to provide a work time in the range of about 45 minutes to about 60 minutes after being mixed with the polyurethane binder precursors and an appropriate foundry aggregate and a strip time that is less than 167% of the work time, as measured from the same starting point.
2. The binder composition of claim 1 , wherein:
the liquid curing catalyst is kept separate from at least the second part of the polyurethane binder precursor until use.
3. The binder composition of claim 1 , wherein:
the liquid curing catalyst further comprises an aromatic hydrocarbon liquid in which the 2-ethanolpyridine is soluble.
4. The binder composition of claim 3 , wherein:
the liquid curing catalyst is present in the aromatic hydrocarbon liquid in an amount of about 20 weight percent.
5. A foundry mix, comprising:
a polyurethane binder precursor, provided in two parts, the first part comprising a polyol component and the second part comprising a polyisocyanate component;
a liquid curing catalyst that is 2-ethanolpyridine present in the range of about 5 to 7 weight percent based on the weight of the first part of the polyurethane binder component; and
an appropriate foundry aggregate.
6. The foundry mix of claim 5 , wherein:
upon mixing the two parts of the polyurethane binder precursor, the liquid curing catalyst and the foundry aggregate, the resulting foundry mix having curing properties characterized by:
a work time in the range of about 45 minutes to about 60 minutes for forming a foundry shape in a pattern; and
a strip time for removing the formed and cured foundry shape from the pattern, such that a ratio of the work time to the strip time is in the range of about 0.6 to 1.0.
7. The foundry mix of claim 5 , wherein:
the liquid curing catalyst is kept separate from at least the second part of the polyurethane binder precursor until use.
8. A “no-bake” process for forming a foundry shape, comprising the steps of:
activating a curing property of a foundry mix according to claim 5 by mixing the two parts of the polyurethane binder precursor with the liquid curing catalyst and the foundry aggregate;
working the activated foundry mix in a pattern to form a foundry shape, the curing rate of the foundry mix allowing the activated foundry mix to be worked for a time of about 45 minutes to about 60 minutes after the activating step; and
stripping the formed foundry shape from the pattern once the formed foundry shape is sufficiently cured to be handleable, the curing rate being sufficient to allow the stripping to occur at a strip time, measured from the activating step, that is less than about 167% of the work time.