Dry mix for composite cement
A dry mix for a composite cement is described. The dry mix includes a calcium-containing material, an aluminum-containing material, a lithium-containing accelerant, a retarder, and a pozzolanic additive that contains a soluble sulfur salt. The pozzolanic additive preferably includes a soluble sulfur salt at a fraction greater than approximately 0.2% by weight. The pozzolanic additive may be a fly ash, and is preferably a class C fly ash. A powdered additive for use with a pre-prepared dry mix for a calcium aluminate cement is also described. The powdered additive includes a lithium-containing accelerant, a retarder, and a pozzolanic additive that contains a soluble sulfur salt.
1. A dry mix for a concrete, consisting of:
from about 80% to about 95% by weight of sand and/or aggregates, and
from about 5% to about 20% by weight of a dry mix for a calcium aluminate composite cement, wherein the dry mix for a calcium aluminate composite cement consists of:
from about 0.01% to about 0.1% by weight of lithium chloride;
from about 0.1% to about 0.5% by weight of a polycarboxylate retarder;
from about 25% to about 40% by weight of class C fly ash, wherein the class C fly ash contains a soluble sulfur salt; and
calcium aluminate cement.
2. The dry mix for a concrete of claim 1 , wherein the class C fly ash includes a soluble sulfur salt at a fraction greater than approximately 0.2% by weight.
3. The dry mix for a concrete of claim 1 , wherein the class C fly ash also contains soluble calcium.
4. The dry mix for a concrete of claim 3 , wherein the class C fly ash contains soluble calcium at a fraction greater than approximately 1% by weight.