METHOD OF MAKING A RUBBER-CONTAINING POLYOLEFIN SEPARATOR
A method of making a rubber-containing polyolefin separator entails preparing a pre-mixture ( 18 ) that includes polyolefin material ( 1 ), silica ( 2 ), and processing oil ( 5 ) and delivering the pre-mixture to a multi-zone extruder ( 12 ) having a sheet die ( 34 ). The pre-mixture becomes partly gelled as it advances in the extruder. Rubber powder ( 6 ) added at a medial zone (Z 4 ) of the extruder combines with the pre-mixture advancing in the extruder to form a gelled rubber-containing extrudate as it exits the sheet die. The extrudate is processed by extracting a portion of the processing oil to form a separator sheet with dispersed rubber powder in the form of domains of larger average size. The larger rubber domains exhibit a smaller average ratio of surface area to volume and thereby results in slower release by diffusion of the beneficial substance from the rubber domains to the battery electrolyte.
1 . A method of making a rubber-containing polyolefin separator, comprising:
preparing a pre-mixture that includes polyolefin material, silica, and processing oil;
delivering the pre-mixture to a multi-zone extruder having a sheet die, the pre-mixture becoming partly gelled as the pre-mixture advances in the extruder;
adding rubber powder at a medial zone of the extruder to combine with the pre-mixture advancing in the extruder, the combined rubber powder and pre-mixture in the form of a gelled rubber-containing extrudate as it exits the sheet die; and
extracting a portion of the processing oil from the extrudate to form a separator sheet with dispersed rubber powder.
2 . The method of claim 1 , in which the silica is a porous silica of a fumed or precipitated type.
3 . The method of claim 2 , in which the rubber powder is a non-porous cured rubber powder.
4 . The method of claim 1 , in which no processing oil is added to the pre-mixture after it is delivered to the extruder.
5 . The method of claim 1 , in which the cured rubber powder does not exceed 10% porosity.
6 . The method of claim 1 , in which the cured rubber powder contains carbon black colorant.
7 . The method of claim 1 , in which the microporous silica-filled polyethylene separator contains a quantity of cured rubber powder of between about 1 wt. % and about 20 wt. % of the weight of the separator.