Process for the preparation of expandable polystyrene
View Patent ↗A process for the preparation of expandable polystyrene (EPS) containing particles of carbon black and/or graphite is disclosed, comprising: (a) forming a masterbatch by adding carbon black and/or graphite to styrene polymer, (b) adding said masterbatch to an organic phase comprising styrene and optional comonomers, and heating the organic phase to a temperature between 30 and 90° C., (c) mixing the organic phase with an aqueous phase comprising water and suspending agents preheated to a temperature between 80 and 120° C. which is higher than the temperature of the organic phase, and (d) polymerizing in a suspension polymerization reaction the styrene and optional comonomers contained in the mixed aqueous and organic phases, with an expanding agent being added before, during or after the polymerization, wherein the styrene polymer in the masterbatch contains at least 1 000 ppm of dimers. The process gives an improved product.
1. Process for the preparation of expandable polystyrene (EPS) containing particles of carbon black and/or graphite, comprising:
(a) forming a masterbatch by adding carbon black and/or graphite to styrene polymer,
(b) adding said masterbatch to an organic phase comprising styrene and optional comonomers, and heating the organic phase to a temperature between 30 and 90° C.,
(c) mixing the organic phase with an aqueous phase comprising water and suspending agents preheated to a temperature between 80 and 120° C. which is higher than the temperature of the organic phase, and
(d) polymerising in a suspension polymerisation reaction the styrene and optional comonomers contained in the mixed aqueous and organic phases, with an expanding agent being added before, during or after the polymerisation,
wherein the masterbatch contains at least 1000 ppm of dimers.
2. Process according to claim 1 , wherein the masterbatch contains at least 1500 ppm of dimers.
3. Process according to claim 1 , wherein the masterbatch contains at least 4000 ppm of oligomers.
4. Process according to claim 1 , wherein any carbon black present has a maximum dimension of no more than 500 nm.
5. Process according to claim 1 , wherein the mixture of polystyrene and carbon black and/or graphite which forms the masterbatch is subjected to a shear rate of at least 40 s −1 prior to addition of the masterbatch to the organic phase.
6. Process according to claim 1 , wherein the masterbatch contains 20-60 wt % of carbon black and/or graphite.
7. Process according to claim 1 , wherein the organic phase following addition of the masterbatch contains 1-15 wt % of carbon black and/or graphite.
8. Process according to claim 1 , wherein the organic phase following addition of the masterbatch contains 2-12 wt % of carbon black and/or graphite.
9. Process according to claim 1 , wherein the organic phase is heated to between 40° C. and 80° C., subject to the condition that the temperature is lower than that of the aqueous phase.
10. Process according to claim 1 , wherein the organic phase is heated to between 45° C. and 70° C., subject to the condition that the temperature is lower than that of the aqueous phase.
11. Process according to claim 1 , wherein the aqueous phase is preheated to a temperature of between 90° C. and 115° C.
12. Process according to claim 1 , wherein the aqueous phase is preheated to a temperature of between 95° C. and 110° C.
13. Process according to claim 1 , wherein the initial polymerisation temperature is 70 to 100° C.
14. Process according to claim 1 , wherein the initial polymerisation temperature is 75 to 95° C.
15. Process according to claim 1 , wherein the initial polymerisation temperature is 80 to 90° C.