Flame retardant adhesive agent composition having improved gas bubble stability, and method for preparing same
Provided is an adhesive agent composition comprising: a copolymer in which a polar functional group-containing monomer is polymerized by the content ratio of 10 weight parts to 50 weight parts with respect to 100 weight parts of a (meth)acrylic acid ester-based monomer; thermally conductive inorganic fillers; and a hollow glass filler or gas bubbles. Also provided is a method for preparing the adhesive agent composition, comprising the steps of: preparing a copolymer by polymerizing a polar functional group-containing monomer by the content ratio of 10 weight parts to 50 weight parts with respect to 100 weight parts of a (meth)acrylic acid ester-based monomer; adding thermally conductive inorganic fillers, a surface-active agent, a photoinitiator, and a photocuring agent to the copolymer to prepare a mixture; and adding a hollow glass filler or injecting gas bubbles into the mixture.
1. An adhesive tape comprising:
an adhesive composition, comprising:
a copolymer in which 14 parts by weight to 25 parts by weight of a polar functional group-containing monomer is polymerized based on 100 parts by weight of a (meth)acrylic acid ester monomer;
thermally conductive inorganic fillers;
hollow glass fillers and bubbles; and
a surfactant including 80% by weight of a siloxane polyalkyleneoxide copolymer and 20% by weight of a non- siloxane polymer,
wherein:
the hollow glass fillers and the bubbles are uniformly dispersed in the adhesive composition,
the thermally conductive inorganic fillers are present in an amount of 50 parts by weight to 300 parts by weight based on 100 parts by weight of the (meth)acrylic acid ester monomer,
the hollow glass fillers are present in an amount of 6 parts by weight to 10 parts by weight based on 100 parts by weight of the (meth)acrylic acid ester monomer,
the surfactant is present in an amount of 5 parts by weight based on 100 parts by weight of the copolymer,
the bubbles are present in an amount of 0.1 vol % to 10 vol % per unit,
the (meth)acrylic acid ester monomer is a C 1 to C 14 alkyl group-containing (meth)acrylic acid ester monomer, and
the copolymer is achieved by thermal polymerization of the (meth)acrylic acid ester monomer and the polar functional group-containing monomer, and
wherein the adhesive tape is manufactured by UV curing of the adhesive composition by coating a thickness of 0.8 mm onto a PET film at a coating temperature of 10° C., and the adhesive tape has 19 to 20 bubbles in an area of 500 μm ×1000 μm of the adhesive tape.
2. The adhesive tape according to claim 1 , wherein the acrylic acid ester monomer comprises at least one selected from the group consisting of methyl (meth)acrylate, ethyl (meth)acrylate, n-propyl (meth)acrylate, isopropyl (meth)acrylate, n-butyl (meth)acrylate, t-butyl (meth)acrylate, sec-butyl (meth)acrylate, pentyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, 2-ethylbutyl (meth)acrylate, n-octyl (meth)acrylate, isooctyl (meth)acrylate, isononyl (meth)acrylate, lauryl (meth)acrylate, tetradecyl (meth)acrylate, and combinations thereof.
3. The adhesive tape according to claim 1 , wherein the polar functional group-containing monomer comprises at least one selected from the group consisting of hydroxyl group-containing monomers, carboxyl group-containing monomers, nitrogen-containing monomers, and combinations thereof.
4. The adhesive tape according to claim 1 , wherein the thermally conductive inorganic fillers have an average particle diameter from 1 μm to 200 μm.
5. The adhesive tape according to claim 1 , wherein the thermally conductive inorganic fillers comprise at least one selected from the group consisting of metal oxide, metal hydroxide, metal nitride, metal carbide, metal boride, and combinations thereof.
6. The adhesive tape according to claim 1 , wherein the hollow glass fillers or the bubbles have a spherical shape.
7. The adhesive tape according to claim 1 , wherein the hollow glass fillers or the bubbles have a diameter of 20 μm to 300 μm.
8. A method for preparing an adhesive tape of claim 1 , comprising:
preparing a copolymer by polymerizing 14 parts by weight to 25 parts by weight of a polar functional group-containing monomer based on 100 parts by weight of a (meth)acrylic acid ester monomer;
preparing a mixture by adding thermally conductive inorganic fillers, a surfactant, a photoinitiator and a photocuring agent to the copolymer; and
adding hollow glass fillers to the mixture and injecting bubbles into the mixture,
wherein
the surfactant includes 80% by weight of a siloxane polyalkyleneoxide copolymer and 20% by weight of a non- siloxane polymer,
the surfactant is present in an amount of 5 parts by weight based on 100 parts by weight of the copolymer,
the thermally conductive inorganic fillers are present in an amount of 50 parts by weight to 300 parts by weight based on 100 parts by weight of the (meth)acrylic acid ester monomer, the hollow glass fillers and the bubbles are uniformly dispersed in the adhesive composition,
the hollow glass fillers are present in an amount of 6 parts by weight to 10 parts by weight based on 100 parts by weight of the (meth)acrylic acid ester monomer, or
the bubbles are present in an amount of 0.1 vol % to 10 vol % per unit,
the adhesive composition has a density of 0.6 g/cm 3 to 1.5 g/cm 3 ,
the (meth)acrylic acid ester monomer is a C 1 to C 14 alkyl group-containing (meth)acrylic acid ester monomer, and
the copolymer is achieved by thermal polymerization of the (meth)acrylic acid ester monomer and the polar functional group-containing monomer, and
curing the mixture comprising the hollow glass fillers and the bubbles therein.