Soft absorbent sandwich web comprising high concentrations of superabsorbent material, cellulosic fibers and surface applied binder

1. Liquid absorbent sandwich web

said web exhibiting in Cartesian coordinates an (x-directional) length along the machine direction of the manufacturing process, further a thickness or z-direction and a width (y-) direction, and comprising as sandwich forming materials

a first and a second outer layer, in the form of an in-situ formed or pre-formed web,

particulate superabsorbent material (SAM),

sandwiched between said outer layers;

individualized fibers adapted to be interspersed between said SAM;

a self-crosslinking latex binder;

the sandwich forming materials being present in the following composition:

SAM from about 70% to about 90%;

fibers interspersed between the SAM from about 5% to 25%;

first outer layer from about 2% to about 15%;

second outer layer from about 2% to about 15%;

self-crosslinking latex binder from about 1% to about 5%;

all as weight-% based on the sum of the weights of the sandwich forming materials,

and wherein said composition is essentially uniform across the x- and y-direction of said web and the SAM particles of the particulate SAM form a particle matrix with the fibers interspersed in interparticle interstices of the particle matrix, and

wherein the particle matrix with the fibers interspersed in interparticle interstices of the particle matrix is formed by compacting the sandwich forming materials in one or more compaction step(s), wherein the maximum line pressure of any of said one or more compaction steps is less than about 60 N/mm and wherein at least one of said compaction steps is executed at a line pressure of more than about 10 N/mm, such that SAM particles are rearranged in a closer and denser relationship while bonding is created between the SAM particles and the fibers,

wherein the self-crosslinking latex binder is applied to at least one of the outer surfaces of said outer layers after the liquid absorbent sandwich web is formed and has undergone the one or more compaction step(s), and

wherein the web exhibits a stiffness to retention capacity ratio as determined by the ratio of the web material stiffness and the area specific capacity, as described herein, of less than 5.0 (mNcm)/(l/m 2 ).

2. A liquid absorbent sandwich web according to claim 1 , wherein said self-crosslinking latex is present in at least one of said first and said second outer layer and in the mixture of said SAM and said fibers between said first and said second outer layers.

3. A liquid absorbent sandwich web according to claim 1 further satisfying at least one of the following concentrations:

SAM from about 80% to about 90%;

fibers interspersed between the SAM from about 8% to 15%;

first outer layer from about 2% to about 10%;

second outer layer from about 2% to about 10%;

self-crosslinking latex binder from about 2% to about 4%.

4. A liquid absorbent sandwich web according to claim 1 , wherein said self-crosslinking latex binder is a vinylacetate-ethylene copolymer.

5. A liquid absorbent sandwich web according to claim 1 , further comprising less than about 5% other binder material, based on the amount of SAM, fibers, and binder.

6. A liquid absorbent sandwich web according to claim 1 , wherein said web exhibits at least one of the following:

an absorbent web centrifuge retention capacity which is at least 23 g/g according to a method as described herein;

an absorbent web centrifuge retention capacity which is at least 85% of the SAM centrifuge retention capacity of the SAM in the web;

a stiffness to retention capacity ratio as determined by the ratio of the web material stiffness and the area specific capacity, as described herein, of less than 3.0, in units of (mNcm)/(l/m 2 ).

7. A disposable absorbent article

comprising a topsheet, a backsheet, and a liquid absorbent sandwich web according to claim 1 positioned between said top sheet and backsheet, further comprising an intermediate layer between said liquid absorbent web and said top sheet.

8. A liquid absorbent sandwich web according to claim 1 , wherein the first and second outer layers comprise cellulosic fibers.

9. A liquid absorbent sandwich web according to claim 1 , wherein the individualized fibers adapted to be interspersed between said SAM comprise cellulosic fibers.

10. A method for making a liquid absorbent sandwich web

said web exhibiting in Cartesian coordinates an (x-directional) length along the machine direction of the manufacturing process, further a thickness or z-direction and a width (y-) direction;

said method comprising

providing as sandwich forming materials

a first and a second outer layer, in the form of an in-situ formed or pre-formed web;

particulate superabsorbent material (SAM);

individualized fibers adapted to be interspersed between said SAM;

a self-crosslinking latex binder;

forming a mixture of said SAM and said individualized fibers,

at a SAM concentration of at least 70% based on the combined weight of SAM and fibers in said mixture;

forming a sandwich structure of said mixture between said first and said second outer layer at an essentially constant thickness, basis weight and concentration along the (x-)-length and (y-) width direction of said web;

compacting said sandwich structure in one or more compaction step(s), wherein a maximum line pressure of any of said one or more compaction step(s) is less than about 60 N/mm and wherein at least one of said compaction step(s) is executed at a line pressure of more than about 10 N/mm such that SAM particles of the particulate SAM are rearranged in a closer and denser relationship while bonding is created between the SAM particles and the fibers, and such that the SAM particles of the particulate SAM form a particle matrix with the fibers interspersed in interparticle interstices of the particle matrix;

applying said self-crosslinking latex binder to at least one of the outer surfaces of said outer layers after the sandwich structure is formed and has undergone the one or more compaction step(s) such that the sandwich forming materials are present in the following composition

SAM from about 70% to about 90%;

fibers interspersed between the SAM from about 5% to 25%;

first outer layer from about 2% to about 15%;

second outer layer from about 2% to about 15%;

self-crosslinking latex binder from about 1% to about 5%;

all as weight-% based on the sum of the weights of the sandwich forming materials;

thermally treating said sandwich structure to reduce moisture content and induce crosslinking of said self-crosslinking latex binder,

wherein the web exhibits a stiffness to retention capacity ratio as determined by the ratio of the web material stiffness and the area specific capacity, as described herein, of less than 5.0 (mNcm)/(l/m 2 ).

11. A method for making a liquid absorbent sandwich web according to claim 10 , wherein the maximum line pressure of any of said one or more compaction steps is less than about 30 N/mm.

12. A method for making a liquid absorbent sandwich web according to claim 10 , wherein at least one of said compaction steps is executed at a line pressure of more than 15 N/mm.

13. A method for making a liquid absorbent sandwich web according to claim 10 , wherein

said self-crosslinking latex binder is applied as an aqueous solution or dispersion at a self-crosslinking latex binder content of more than 5% and less than about 30%, all based on dry matter of the latex binder in the solution or dispersion.

14. A method for making a liquid absorbent sandwich web according to claim 10 , wherein said thermal treatment of said sandwich web is at between 130° C. and 180° C.

15. A method for making a liquid absorbent sandwich web according to claim 10 , wherein said thermal treatment is executed until a final overall moisture content of said absorbent web is less than 15%.

16. A method for making a liquid absorbent sandwich web according to claim 10 , wherein the first and the second outer layers comprise cellulosic fibers.

17. A method for making a liquid absorbent sandwich web according to claim 10 , wherein the individualized fibers adapted to be interspersed between said SAM comprise cellulosic fibers.

18. A method for the making of a liquid absorbent sandwich web according to claim 10 , wherein said self-crosslinking latex binder is applied to at least one of the outer surfaces of said outer layers such that the self-crosslinking latex binder is present in the sandwich forming materials at an amount of at least 2% and not more than 4%, based on the dry amount of latex binder in the absorbent web.

19. A method for making a liquid absorbent sandwich web according to claim 10 , comprising

applying said self-crosslinking latex binder to said mixture of said SAM and said individualized fibers.

20. A method for making a liquid absorbent sandwich web according to claim 10 , comprising

applying vacuum suction z-directionally through said sandwich structure.