Block copolymer composition for viscous adhesive, and adhesive composition
It is an object to provide a block copolymer composition for a viscous adhesive, which will be a viscous adhesive composition excellent in balance of the adhesive properties such as tack strength and tackiness, having a low melt viscosity, and excellent solubility, coating properties, ejection stability, and surface skin quality. The block copolymer composition for a viscous adhesive having: a component (a) in an amount of 50 mass % or more and 90 mass % or less; and a component (b) in an amount of 10 mass % or more and 50 mass % or less; a content of the vinyl aromatic monomer unit being 25 to 50 mass %; a viscosity of the 15 mass % toluene solution being 10 to 40 mPa·s; and a number average molecular weight ratio of the component (b) to the component (a) being 2.0 to 4.0.
1. A block copolymer composition for as viscous adhesive comprising:
a component (a): more than 80 mass % and 90 mass % or less of a block copolymer having a number average molecular weight of 30,000 or more and 60,000or less, comprising a polymer block (A) mainly including a vinyl aromatic monomer unit and a polymer block (B) mainly including a conjugated diene monomer unit selected from the group consisting of 1,3-butadiene, 2,3-dimethy 1,3-butadiene, 1,3-pentadiene, and 3-hexacliene; and
a component (b): 10 mass % or more and less than 20 mass % of a block copolymer having a number average molecular weight of more than 120,000 and 200,000 or less comprising a polymer block (A) mainly including a vinyl aromatic monomer unit and a polymer block (B) mainly including a conjugated diene monomer unit selected from the group consisting of 1,3- butadiene, 2,3-dimethyl-1,3-butadiene, 1,3-pentadiene, and 1,3-hexadiene;
a content of the vinyl aromatic monomer unit being 25 to 50 mass %;
the composition having a 15 mass % toluene solution viscosity of 10 to 40 mPas; and
a number average molecular weight ratio of the component (b) to the component (a) being 2.0 to 4.0.
2. The block copolymer composition for the viscous adhesive according to claim 1 , wherein
the component (a) is a diblock copolymer represented by a formula (A-B); and
the component (b) is a tribranch block copolymer represented by a formula (A-B)3X, wherein X represents a residue of a coupling agent or a residue of a polymerization initiator.
3. The block copolymer composition for the viscous adhesive according to claim 1 , wherein the number average molecular weight ratio of the component (b) to the component (a) is 2.3 to 3.6.
4. The block copolymer composition for the viscous adhesive according to claim 1 , wherein the number average molecular weight of the component (b) is 130,000 or more and 200,000 or less.
5. The block copolymer composition for the viscous adhesive according to claim 1 , wherein the number average molecular weight of the component (b) is 160,000 or more and 200,000 or less.
6. A viscous adhesive composition comprising:
the block copolymer composition for the viscous adhesive according to claim 1 in an amount of 100 parts by mass;
a tackifier in an amount of 100 to 400 parts by mass; and
a softener in an amount of 50 to 150 parts by mass.
7. A block copolymer composition for a viscous adhesive comprising:
a component (a):50 mass % or more and 90 mass % or less of as block copolymer having a number average molecular weight of 40,000 or more and 60,000 or less, comprising a polymer block(A) mainly including a vinyl aromatic monomer unit and a polymer block (B) mainly including a conjugated diene monomer unit selected from the group consisting of 1,3-butadiene, 2,3-dimethyl-1,3-butadiene, 1,3-pentadiene, and 1,3-hexadiene; and
a component (b): 10 mass % or more and 50 mass % or less of a block copolymer having a number average molecular weight of 160,000 or more and 200,000 or less, comprising a polymer block (A) mainly including a vinyl aromatic monomer unit and a polymer block (B) mainly including a conjugated diene monomer unit selected from the group consisting of 1,3-butadiene, 2,3-dimethyl-1,3-butadiene, 1,3-pentadiene, and 1,3-hexacliene;
a content of the vinyl aromatic monomer unit being 25 to 50 mass %;
the composition having a 15 mass % toluene solution viscosity of 10 to 40 mPa s; and
a number average molecular weight ratio of the component (b) to the component (a) being 2.0 to 4.0.
8. The block copolymer composition for the viscous adhesive according to claim 7 , wherein
the component (a) is a diblock copolymer represented by a formula (A-B); and
the component (b) is a tribranch block copolymer represented by a formula (A-B)3X, wherein X represents a residue of a coupling agent or a residue of a polymerization initiator.
9. The block copolymer composition for the viscous adhesive according to claim 7 , wherein the number average molecular weight ratio of the component (b) to the component (a) is 2.3 to 3.6.
10. The block copolymer composition for the viscous adhesive according to claim 7 , wherein the content of the component (a) is 50 mass % or more and 80 mass % or less; and the content of the component (b) is 20 mass % or more and 50 mass % or less.
11. A viscous adhesive composition comprising:
the block copolymer composition for the viscous adhesive according to claim 7 in an amount of 100 parts by mass;
a tackifier in an amount of 100 to 400 parts by mass; and
a softener in an amount of 50 to 150 parts by mass.