Abradable coating made of a material having a low surface roughness
View Patent ↗The present invention relates to an abradable coating for a turbine engine part, characterized by the fact that said coating includes a layer made of an abradable material, the surface asperities of which are filled with thermally bonded ceramic grains, forming a smooth, free surface having a low roughness.
1. A turbine engine part, comprising at least one stator part, and a rotating part, the rotating part inside the stator part or facing the stator part, the at least one stator part comprises an internal face that comprises a layer of a MCrAlY abradable coating wherein M is selected from the group consisting of Ni, Co, NiCo, and CoNi, wherein the layer of the MCrAlY alloy forms a seal between the stator part and the rotating part,
wherein the layer of the abradable coating has surface irregularities filled in by thermally bound ceramic grains that are alumina, wherein the ceramic grains penetrate the layer of the abradable coating over a depth of between 50 and 1000 μm, wherein the ceramic grains are bound by partial sintering, wherein a ceramic grain size is less than 1 μm, wherein the layer of the abradable coating has a surface roughness of less than 1 μm and wherein a free surface of the layer of the abradable coating comprises portions of the MCrAlY alloy and the alumina.
2. The turbine engine part of claim 1 , wherein M is Ni.
3. The turbine engine part of claim 1 , wherein M is Co.
4. The turbine engine part of claim 1 , wherein M is NiCo.
5. The turbine engine part of claim 1 , wherein M is CoNi.
6. The turbine engine part of claim 1 , wherein the MCrAlY abradable coating further comprises a porogenic agent.