NOVEL HYDROXYALKYL METHYL CELLULOSE ACETATE SUCCINATES
Novel hydroxyalkyl methyl cellulose acetate succinates which a) have from 4.0 to less than 10.0 weight percent of succinoyl groups, b) have a weight average molecular weight M w of from 80,000 Dalton to 350,000 Dalton, and c) exhibit a turbidity of up to 41 NTU as a 1.5 weight percent solution in acetone; and novel hydroxyalkyl methyl cellulose acetate succinates which a) have from 10.0 to 20.0 weight percent of succinoyl groups, b) have a weight average molecular weight M w of from 80,000 Dalton to 350,000 Dalton, and c) exhibit a turbidity of up to 37 NTU as a 1.5 weight percent solution in acetone are useful for preparing solid dispersion of active ingredients in these hydroxyalkyl methyl cellulose acetate succinates.
1 . A hydroxyalkyl methyl cellulose acetate succinate
a) having from 4.0 to less than 10.0 weight percent of succinoyl groups,
b) having a weight average molecular weight M w of from 80,000 Dalton to 350,000 Dalton, measured by SEC-MALLS using as mobile phase a mixture of 40 parts by volume of acetonitrile and 60 parts by volume of aqueous buffer containing 50 mM NaH 2 PO 4 and 0.1 M NaNO 3 ,
c) exhibiting a turbidity of up to 41 NTU as a 1.5 weight percent solution in acetone, measured according to USEPA method 180.1,
and
d) having a viscosity of up to 4.0 mPa·s, measured as a 2.0 wt % solution of the esterified cellulose ether in 0.43 wt.-% aqueous NaOH at 20° C. according to an Ubbelohde measurement according to DIN 51562-1:1999-01.
2 . The hydroxyalkyl methyl cellulose acetate succinate of claim 1 exhibiting a turbidity of up to 37 NTU as a 1.5 weight percent solution in acetone.
3 . The hydroxyalkyl methyl cellulose acetate succinate of claim 1 having e) from 10.0 to 14.0 weight percent of acetyl groups.
4 . A hydroxyalkyl methyl cellulose acetate succinate
a) having from 10.0 to 20.0 weight percent of succinoyl groups,
b) having a weight average molecular weight M w of from 80,000 Dalton to 350,000 Dalton, measured by SEC-MALLS using as mobile phase a mixture of 40 parts by volume of acetonitrile and 60 parts by volume of aqueous buffer containing 50 mM NaH 2 PO 4 and 0.1 M NaNO 3 ,
c) exhibiting a turbidity of up to 37 NTU as a 1.5 weight percent solution in acetone, measured according to USEPA method 180.1,
and
d) having a viscosity of up to 4.0 mPa·s, measured as a 2.0 wt % solution of the esterified cellulose ether in 0.43 wt.-% aqueous NaOH at 20° C. according to an Ubbelohde measurement according to DIN 51562-1:1999-01.
5 . The hydroxyalkyl methyl cellulose acetate succinate of claim 4 having e) from 5.0 to 11.0 weight percent of acetyl groups.
6 . The hydroxyalkyl methyl cellulose acetate succinate of claim 1 exhibiting a turbidity of from 10 to 30 NTU.
7 . A composition comprising a liquid diluent and at least one hydroxyalkyl methyl cellulose acetate succinate of claim 1 .
8 . (canceled)
9 . A solid dispersion comprising at least one active ingredient in at least one hydroxyalkyl methyl cellulose acetate succinate of claim 1 .
10 . The solid dispersion of claim 9 in the form of strands, pellets, granules, pills, tablets, caplets, microparticles, fillings of capsules or injection molded capsules or in the form of a powder, film, paste, cream, suspension or slurry.
11 . A process for producing the solid dispersion of claim 9 comprising the steps of blending a) at least one hydroxyalkyl methyl cellulose acetate succinate of claim 1 , b) one or more active ingredients and c) one or more optional additives, and subjecting the blend to extrusion.
12 . A process for producing the solid dispersion of claim 9 comprising the steps of blending a) at least one hydroxyalkyl methyl cellulose acetate succinate of claim 1 , b) one or more active ingredients, c) one or more optional additives, and d) a liquid diluent to prepare a liquid composition, and removing said liquid diluent.
13 . The process of claim 12 wherein the liquid composition is subjected to spray-drying.
14 . A dosage form being coated with the hydroxyalkyl methyl cellulose acetate succinate of claim 1 .
15 . A capsule shell comprising the hydroxyalkyl methyl cellulose acetate succinate of claim 1 .
16 . A composition comprising a liquid diluent and at least one hydroxyalkyl methyl cellulose acetate succinate of claim 4 .
17 . A solid dispersion comprising at least one active ingredient in at least one hydroxyalkyl methyl cellulose acetate succinate of claim 4 .
18 . A process for producing the solid dispersion of claim 17 comprising the steps of blending a) at least one hydroxyalkyl methyl cellulose acetate succinate of claim 4 , b) one or more active ingredients and c) one or more optional additives, and subjecting the blend to extrusion.
19 . process for producing the solid dispersion of claim 17 comprising the steps of blending a) at least one hydroxyalkyl methyl cellulose acetate succinate of claim 4 , b) one or more active ingredients, c) one or more optional additives, and d) a liquid diluent to prepare a liquid composition, and removing said liquid diluent.
20 . A dosage form being coated with the hydroxyalkyl methyl cellulose acetate succinate of claim 4 .
21 . A capsule shell comprising the hydroxyalkyl methyl cellulose acetate succinate of claim 4 .