Strapping adhesive tape
The invention relates to an adhesive tape carrier made of a film, onto at least one side of which film an adhesive material is applied, wherein the film is a monoaxially stretched film made of polypropylene which contains at least 80 percent by weight polypropylene which has been processed in advance at least once, preferably has been extruded at least once, wherein the film has a stretching ratio during stretching in the longitudinal direction of 1:4 to 1:10.
1. A method of preparing an adhesive tape, said method comprising:
(a) melting polypropylene including at least 80 wt % of polypropylene which has been processed at least once before, and optionally has been extruded, said melting resulting in polypropylene melt;
(b) extruding the polypropylene melt to form a film;
(c) monoaxially drawing the film with a draw ratio in the longitudinal direction of 1:4 to 1:10; and
(d) coating the film with a pressure-sensitive adhesive;
wherein the film after drawing exhibits at least one property that is not substantially changed compared to that exhibited by a comparison film prepared in the same manner except from 100 wt % virgin polypropylene, wherein the at least one property is selected from the group consisting of stress at 1% strain, stress at 10% strain, tensile strength, and elongation at break.
2. The method according to claim 1 , wherein the polypropylene which has been processed at least once before has been extruded at least once before.
3. The method of claim 1 ,
wherein
a thickness of the film is between 20 and 2000 μm.
4. The method of claim 1 ,
wherein
the draw ratio on drawing in the longitudinal direction is 1:5 to 1:9.
5. The method of claim 1 ,
wherein
the pressure-sensitive adhesive is selected from the group consisting of natural rubbers, blends of natural rubbers, synthetic rubbers, and mixtures thereof.
6. The method of claim 1 ,
wherein
the pressure-sensitive adhesive comprises tackifier resins.
7. The method of claim 1 ,
wherein the pressure-sensitive adhesive comprises an additive selected from the group consisting of at least one UV protectant, other blending components, and mixtures thereof.
8. The method of claim 2 ,
wherein
a fraction in the film of polypropylene which has been extruded at least once is at least 85 wt %.
9. The method according to claim 1 , wherein the polypropylene that is melted in (a) is composed 100% of polypropylene which has been processed at least once before, and optionally has been extruded.
10. The method according to claim 2 , wherein the polypropylene that is melted in (a) is composed 100% of polypropylene which has been processed at least once before, and has been extruded at least once before.
11. The method according to claim 1 , wherein the adhesive tape is an adhesive strapping tape.
12. The method according to claim 11 , wherein the polypropylene is a polypropylene homopolymer or polypropylene/polyethylene copolymer having a melt index (MFI) between 0.5 to 2.
13. The method according to claim 12 , wherein the polypropylene is a polypropylene block copolymer having MFI of 1.5 g/10 min, flexural modulus of 1280 MPa, and a crystallite melting point of 164° C.;
wherein steps (b) and (c) are carried out on a single-screw extrusion unit with a flat die with flexible die lip in one layer, followed by a chill roll station, and a single-stage short-gap drawing unit;
wherein said die operates at a temperature of 230° C.; and
wherein said drawing unit draws the film in a draw ratio of 1:6.5.