Hard coating film

1. A hard coating film, comprising:

a first hard coating layer having a first elastic modulus; and

a second hard coating layer being directly in contact with the first hard coating layer and having a second elastic modulus,

wherein a difference between the first and second elastic moduli is 500 MPa or more, and

wherein the first elastic modulus is 300 to 1,500 MPa, and the second elastic modulus is 2,000 to 3,500 MPa, as measured according to ASTM D882,

wherein the first and second hard coating layers independently have a thickness of 50 to 500 μm, and

wherein the hard coating film exhibits a pencil hardness of 7H or more at a load of 1 kg.

2. The hard coating film of claim 1 , wherein the difference between the first and second elastic moduli is 500 to 3,000 MPa.

3. The hard coating film of claim 1 , wherein the first hard coating layer comprises a first photocurable crosslinking copolymer of a first photocurable elastic polymer and a mono- to hexa-functional acrylate monomer, and the second coating layer comprises a second photocurable crosslinking copolymer of a second photocurable elastic polymer and a tri- to hexa-functional arylate monomer, and inorganic microparticles dispersed in the second photocurable crosslinking copolymer.

4. The hard coating film of claim 3 , wherein the first and the second photocurable elastic polymers are the same or different, and independently have an elongation of 15 to 200%, as measured according to ASTM D638.

5. The hard coating film of claim 3 , wherein the first and the second photocurable elastic polymers are the same or different, and independently comprise at least one selected from the group consisting of a polycaprolactone, a urethane acrylate polymer and a polyrotaxane.

6. The hard coating film of claim 5 , wherein the polyrotaxane comprises a cyclic moiety (macrocycle) in which lactone compounds with a (meth)acrylate moiety conjugated to the end thereof are bonded each other; a thread moiety held within the macrocycle; and stoppers provided at both ends of the thread moiety so as to prevent dissociation of the macrocycle.

7. The hard coating film of claim 3 , wherein the first hard coating layer includes the first photocurable elastic polymer in an amount of 20 to 80 weight parts and the mono- to hexa-functional acrylate monomer in an amount of 80 to 20 weight parts, based on 100 weight parts of the first hard coating layer.

8. The hard coating film of claim 3 , wherein the second hard coating layer includes 5 to 20 weight parts of the second photocurable elastic polymer polymerized with 80 to 95 weight parts of the tri- to hexa-functional acrylate monomer, based on 100 weight parts of the second photocurable crosslinking copolymer.

9. The hard coating film of claim 3 , wherein the second hard coating layer includes the second photocurable crosslinking copolymer in an amount of 40 to 90 weight parts, and the inorganic microparticles in an amount of 10 to 60 weight parts, based on 100 weight parts of the second hard coating layer.

10. The hard coating film of claim 3 , wherein the mono- to hexa-functional acrylate monomer includes at least one selected from the group consisting of hydroxyethylacrylate (HEA), hydroxyethylmethacrylate (HEMA), hexandiol dicrylate (HDDA), tripropylene glycol dicrylate (TPGDA), ethylene glycol dicrylate (EGDA), trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxytriacrylate (TMPEOTA), glycerin propoxylated triacrylate (GPTA), pentaerythritol tetraacrylate (PETA), and dipentaerythritol hexaacrylate (DPHA).

11. The hard coating film of claim 3 , wherein the tri- to hexa-functional acrylate monomer includes at least one selected from the group consisting of trimethylolpropane triacrylate (TMPTA), trimethylolpropane ethoxytriacrylate (TMPEOTA), glycerin propoxylated triacrylate (GPTA), pentaerythritol tetraacrylate (PETA), dipentaerythritol hexaacrylate (DPHA), and a combination thereof.

12. The hard coating film of claim 1 , further comprising on the first hard coating layer or the second hard coating layer at least one layer selected from the group consisting of a plastic resin film, an adhesive film, an releasable film, an electrically conductive film, an electrically conductive layer, a curable resin layer, a non-conductive film, a metal mesh layer, and a patterned metal layer.

13. The hard coating film of claim 12 , wherein the plastic resin film comprises at least one selected from polyethyleneterephtalate (PET), ethylene vinyl acetate (EVA), cyclic olefin polymer (COP), cyclic olefin copolymer (COC), polyacrylate (PAC), polycarbonate (PC), polyethylene (PE), polymethylmethacrylate (PMMA), polyetheretherketon (PEEK), polyethylenenaphthalate (PEN), polyetherimide (PEI), polyimide (PI), triacetylcellulose (TAC), MMA (methyl methacrylate) and a fluoro-polymer.

14. The hard coating film of claim 1 , wherein the hard coating film does not crack when a 22 g steel ball is freely dropped 10 times thereon from a height of 50 cm.

15. The hard coating film of claim 1 , wherein the hard coating film allows two or less scratches to appear thereon after it is doubly rubbed 400 times with a steel wool #0000 under a load of 500 g.

16. The hard coating film of claim 1 , having a light transmittance of 91% or more, a haze of 0.4 or less and a color b* value of 1.0 or less.

17. The hard coating film of claim 1 , wherein the hard coating film has a color b* value after exposure to UV B for 72 hrs which differs from a pre-exposed, color b* value by 0.5 or less.

18. The hard coating film of claim 1 , wherein when the hard coating film is disposed on a plane after exposure to a temperature of 50° C. or more at a humidity of 80% or more for 70 hrs or more, each edge or side of the hard coating film is spaced apart from the plane by 1.0 mm or less, maximally.