Method of determining the non-propagation threshold of fatigue cracks at high frequency
A method of determining the non-propagation threshold of fatigue cracks at high frequency, wherein cyclic loading is exerted on at least one testpiece having an elliptical hole in a testpiece zone, the elliptical hole having a notch at one end and the testpiece being held between two rigid masses with two rigid pre-stress plates being arranged on either side of the at least one testpiece and each fastened at its two ends to the two rigid masses, which cyclic loading is at a frequency that is selected as being equal to the resonant frequency of the assembly including the testpiece, the masses, and the stress plates, so as to generate a fatigue crack from the notch, and then once it has been observed that the crack has stopped propagating, the final length of the crack is measured and a chart is used to determine the non-propagation threshold.
1. A method of determining a non-propagation threshold for fatigue cracks, comprising:
initiating a fatigue crack by cyclic loading on at least one testpiece having an elliptical hole in a test zone, the elliptical hole having a notch at an apex of the elliptical hole for initiating a fatigue crack and the testpiece being held between two rigid masses with two rigid pre-stress plates being arranged on either side of said at least one testpiece and each fastened at its two ends to said two rigid masses, which cyclic loading is obtained by an electrodynamic vibrator pot securely fastened by rigid uprights to a structure supporting said two rigid masses and including a thrust rod for transmitting said cyclic loading to an assembly comprising the at least one testpiece, the two rigid masses, and the two rigid pre-stress plates, at a frequency that is selected as being equal to the resonant frequency of said assembly, so as to generate said fatigue crack from said notch;
determining that the fatigue crack has stopped propagating;
measuring a final length of the fatigue crack; and
using a chart showing a decay rate of ΔK th function of crack length to determine said threshold ΔK th for non-propagation of fatigue cracks.
2. The method according to claim 1 , wherein said determining that the crack has stopped comprises counting a predetermined number of loading cycles.
3. The method according to claim 2 , wherein said predetermined number lies from 8 million to 12 million loading cycles.
4. The method according to claim 1 , wherein said cyclic loading lies at a frequency from 300 Hz to 2000 Hz.
5. The method according to claim 1 , further comprising varying the cyclic loading frequency by modifying said resonant frequency.
6. The method according to claim 1 , wherein said notch is made at one end of the major axis of said elliptical hole and in a direction of said loading.
7. The method according to claim 1 , further comprising initially putting said at least one testpiece into compression by traction on said two pre-stress plates with progressively reducing clearance that exists initially between one of said ends of said two pre-stress plates and a facing one of said two rigid masses.
8. The method according to claim 1 , wherein said uprights are rigid brackets.
9. The method according to claim 1 , wherein the decay rate is expressed as ΔK(x)/ΔKo=exp(−0.08x), in which x is a distance between a tip of the crack and an edge of the elliptical hole in millimeters, and ΔKo is a maximum amplitude reached by ΔK close to the elliptical hole.
10. A method of determining a non-propagation threshold for fatigue cracks, comprising:
generating at least one testpiece having an elliptical hole in a test zone, the elliptical hole having a notch made at an apex in a direction of a cyclic loading;
initiating a fatigue crack from said notch by said cyclic loading at a predetermined frequency on said at least one testpiece;
when the fatigue crack has stopped propagating, stopping the cyclic loading;
measuring a final length of the fatigue crack; and
using a chart showing a decay rate of ΔK th function of crack length to determine a threshold ΔK th for non-propagation of fatigue cracks.