INNOVATIVE HYDROPHILIC POLYISOCYANATES WITH IMPROVED STORAGE STABILITY
The invention relates to innovative, water-dispersible, hydrophilic polyisocyanates and polyisocyanate mixtures, to a process for preparing them, to compositions comprising the hydrophilic polyisocyanates of the invention, and to their use as a starting component in the production of polyurethane plastics, more particularly as crosslinkers for water-soluble or water-dispersible film-forming, adhesives or sealant binders or binder components having groups which are reactive towards isocyanate groups.
1 . A method for preparing a hydrophilic polyisocyanate, the method comprising:
reacting a prepolymer which carries uretdione groups, with at least one emulsifier, the emulsifier comprising an ionogenic group which
in the case of an acidic ionogenic group in water has a pK a >8 at room temperature or
in the case of a basic ionogenic group has a pK b >8 at room temperature.
2 . The method according to claim 1 ,
the emulsifier being at least one compound selected from the group consisting of sulphonates and phosphates.
3 . The method according to claim 1 , the emulsifier being at least one sulphonate selected from the group consisting of hydroxyalkylsulphonates, hydroxypolyethersulphonates, aminoalkylsulphonates and aminopolyethersulphonates.
4 . The method according to claim 1 , further comprising:
reacting a polyisocyanate which carries uretdione groups with a monomeric, oligomeric and/or polymeric compound which contains a hydroxyl group, thereby obtaining the prepolymer.
5 . The method according to claim 1 , the prepolymer having a free NCO content in the range from 0.2 wt % to 20 wt % based on the total weight of the prepolymer.
6 . A hydrophilic polyisocyanate having at least one uretdione group, the hydrophilic polyisocyanate comprising an internal emulsifier.
7 . (canceled)
8 . A composition comprising:
the hydrophilic polyisocyanate according to claim 7 and
optionally water.
9 . The composition according to claim 8 , further comprising:
a reactant for the hydrophilic polyisocyanate, said reactant containing a hydroxyl group and being dispersed, emulsified or dissolved in water, and
optionally an auxiliary and/or adjuvant and
optionally a catalyst.
10 . The composition according to claim 9 , the reactant being selected from the group consisting of polyethers, polyesters, polycarbonates, polyalkyd resins, polyacrylates, polyurethanes and polycaprolactones.
11 . A polyurethane plastic, comprising:
the hydrophilic polyisocyanate according to claim 6 .
12 . An article, comprising:
the hydrophilic polyisocyanate according to claim 6 ,
wherein the article is a crosslinker for water-soluble or water-dispersible film forming binders, adhesives binders or sealant binders or binder components having groups which are reactive towards isocyanate groups.
13 . A polyurethane plastic, comprising:
the composition according to claim 8 .
14 . A coating, adhesive bond or sealant, comprising:
a composition comprising the hydrophilic polyisocyanate according to claim 6 .
15 . A method for producing a coating, adhesive bond or sealant, the method comprising:
applying a composition comprising the hydrophilic polyisocyanate according to claim 6 .
16 . The method according to claim 4 ,
the monomeric, oligomeric and/or polymeric compound being selected from the group consisting of polyesters, polythioethers, polyethers, polycaprolactams, polyepoxides, polyesteramides, polyurethanes, low molecular weight dialcohols, low molecular weight trialcohols, low molecular weight tetraalcohols and monoalcohols.
17 . The method according to claim 5 ,
the prepolymer having a uretdione group content of 0.5 to 25 wt %, based on the total weight of the prepolymer.