Adhesives and related methods

1. A cure in place adhesive comprising:

5-70 wt % of a bodying component comprising a pre-polymerized (meth)acrylic backbone base polymer having a molecular weight (Mw) of 5,000 to 1,000,000;

0-40 wt % of at least one structural diluent;

30-95 wt % of at least one radical addition diluent;

0-10.0 wt % curative;

0-10 wt % photoinitiator;

0-10 wt % photosensitizer; and

0-10 wt % stabilizer,

wherein the radical addition diluent is selected from the group consisting of epoxy acrylate monomer (ACE™ hydroxyl acrylate), isostearyl acrylate, heptadecyl acrylate, dicyclopentadiene acrylate, 3-ethyl-3-(methyl acrylate) oxetane (OXE-10), 3-ethyl-3-(methyl methacrylate) oxetane (OXE-30), 3,4-epoxycyclohexyl methyl methacrylate (S-100), acrylic macromer having a molecular weight (Mw) of less than 10,000 daltons, 2-acryloyloxypropyl phthalate (V2100), 1,2-cyclohexanedicarboxylic add, mono[1-methyl-2-[(1-oxo-2-propenyl)oxy]ethyl] ester (cycloaliphatic V2100), polyalkyl methacrylate (PAMA), alkoxylated tetrahydrofurfuryl (THF) acrylate of the following formula (1), tetrahydrofurfuryl acrylate (THFA or THF acrylate) of the following formula (4), and urethane acrylates having a molecular weight (Mw) of less than 2000 daltons,

2. The adhesive of claim 1 wherein the pre-polymerized (meth)acrylic backbone base polymer has a Mw of 15,000 to 250,000.

3. The adhesive of claim 2 wherein the pre-polymerized (meth)acrylic backbone base polymer has a Mw of 15,000 to 100,000.

4. The adhesive of claim 1 wherein the cure in place adhesive is a pressure sensitive adhesive.

5. The adhesive of claim 1 wherein the bodying component is selected to be non-reactive with the radical addition diluent when the radical addition diluent is exposed to a stimulus.

6. The adhesive of claim 5 wherein the stimulus is selected from the group consisting of radiation, heat, moisture, pressure, ultrasound, chemical exposure, and combinations thereof.

7. The adhesive of claim 1 further comprising at least one structural diluent, wherein the structural diluent is selected from the group consisting of 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexanecarboxylate (S-21), Bis[(3,4-epoxycyclohexyl)methyl]adipate (S-28), difunctional bisphenol A/epichlorohydrin derived liquid epoxy resin (Epon 828), Bisphenol A epoxy resin having a weight per epoxide of 235-263 g/eq as measured by ASTM D1652 (Epon 834), beta-(3,4-epoxycyclohexyl)ethyltrimethoxysilane (A-186), gamma-glycidoxypropyltrimethoxysilane (A-187), glycidyl ester of neodecanoic acid (EP-10), isocyante-functional urethane acrylate (Desmolux D100), isocyanate-bearing urethane acrylate (Desmolux D200), aliphatic polyisocyanate (low-viscosity hexamethylene diisocyanate (HDI) biuret) (Desmodur N3200), aliphatic polyisocyanate (hexamethylene diisocyanate (HDI) biuret) (Desmodur N100), aliphatic polyisocyanate (hexamethylene diisocyanate (HDI) trimer) (Desmodur N3300), poly(propylene oxide) (PPO) oligomer having a molecular weight (Mw) of less than 5,000 daltons, trimethylolpropane oxetane (TMPO), poly(ethylene oxide) (PEO) oligomer having a molecular weight (Mw) of less than 5,000 daltons, ethyl hexyl oxetane (2EH oxetane), difunctional oxetane, trimethylolpropane triacrylate (TMPTA) of the following formula (5), tripropyleneglycol diacrylate (TPGDA) of the following formula (6), ethoxylated bisphenol A diacrylate of the following formula (7) in which n+m=3, ethoxylated trimethylolpropane triacrylate of the following formula (8), bisphenol A diglycidyl ether diacrylate of the following formula (9), 1,2-cyclic ethers, 1,3-cyclic ethers, 1,4-cyclic ethers, anhydrides, lactones, lactams, cyclic ethers, siloxanes, oxazolines, oxalidines, and bismaleimides;

8. The adhesive of claim 1 exhibiting a subsequent thermoplastic adhesive state when the radical addition diluent polymerizes upon exposure to a stimulus.

9. The adhesive of claim 1 further comprising at least one structural diluent, wherein the structural diluent is selected from the group consisting of 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexanecarboxylate (S-21), Bis[(3,4-epoxycyclohexyl)methyl]adipate (S-28), difunctional bisphenol A/epichlorohydrin derived liquid epoxy resin (Epon 828), Bisphenol A epoxy resin having a weight per epoxide of 235-263 g/eq as measured by ASTM D1652 (Epon 834), beta-(3,4-epoxycyclohexyl)ethyltrimethoxysilane (A-186), gamma-glycidoxypropyltrimethoxysilane (A-187), glycidyl ester of neodecanoic acid (EP-10), isocyanate-functional urethane acrylate (Desmolux D100), isocyanate-bearing urethane acrylate (Desmolux D200), aliphatic polyisocyanate (low-viscosity hexamethylene diisocyanate (HDI) biuret) (Desmodur N3200), aliphatic polyisocyanate (hexamethylene diisocyanate (HDI) biuret) (Desmodur N100), aliphatic polyisocyanate (hexamethylene diisocyanate (HDI) trimer) (Desmodur N3300), poly(propylene oxide) (PPO) oligomer having a molecular weight (Mw) of less than 5,000 daltons, trimethylolpropane oxetane (TMPO), poly(ethylene oxide) (PEO) oligomer having a molecular weight (Mw) of less than 5,000 daltons, ethyl hexyl oxetane (2EH oxetane), difunctional oxetane, ethoxylated bisphenol A diacrylate of the following formula (7) in which n+m=3, ethoxylated trimethylolpropane triacrylate of the following formula (8), bisphenol A diglycidyl ether diacrylate of the following formula (9), 1,2-cyclic ethers, 1,3-cyclic ethers, 1,4-cyclic ethers, anhydrides, lactones, lactams, cyclic ethers, siloxanes, oxazolines, oxalidines, and bismaleimides;

10. The adhesive of claim 1 further comprising at least one structural diluent, wherein the structural diluent is selected from the group consisting of 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexanecarboxylate (S-21), Bis[(3,4-epoxycyclohexyl)methyl]adipate (S-28), difunctional bisphenol A/epichlorohydrin derived liquid epoxy resin (Epon 828), Bisphenol A epoxy resin having a weight per epoxide of 235-263 g/eq as measured by ASTM D1652 (Epon 834), beta-(3,4-epoxycyclohexyl)ethyltrimethoxysilane (A-186), gamma-glycidoxypropyltrimethoxysilane (A-187), glycidyl ester of neodecanoic acid (EP-10), isocyanate-functional urethane acrylate (Desmolux D100), isocyanate-bearing urethane acrylate (Desmolux D200), aliphatic polyisocyanate (low-viscosity hexamethylene diisocyanate (HDI) biuret) (Desmodur N3200), aliphatic polyisocyanate (hexamethylene diisocyanate (HDI) biuret) (Desmodur N100), aliphatic polyisocyanate (hexamethylene diisocyanate (HDI) trimer) (Desmodur N3300), poly(propylene oxide) (PPO) oligomer having a molecular weight (Mw) of less than 5,000 daltons, trimethylolpropane oxetane (TMPO), poly(ethylene oxide) (PEO) oligomer having a molecular weight (Mw) of less than 5,000 daltons, ethyl hexyl oxetane (2EH oxetane), difunctional oxetane, ethoxylated bisphenol A diacrylate of the following formula (7) in which n+m=3, ethoxylated trimethylolpropane triacrylate of the following formula (8), bisphenol A diglycidyl ether diacrylate of the following formula (9), 1,2-cyclic ethers, 1,3-cyclic ethers, 1,4-cyclic ethers, butyrolactone, valerolactone, caprolactone, methy-butyrolactone, butyrolactam, valerolactam, caprolactam, cyclic ethers, siloxanes, oxazolines, oxalidines, bismaleimides,

and

lactones of the following formulas (10)-(12)

wherein n is 4 or 5, h, i, k, and m are independently 1 or 2 and each R is independently chosen from H or hydrocarbyl containing up to 12 carbon atoms.

11. The adhesive of claim 1 wherein the adhesive comprises 0.001-10.0 wt % curative.

12. A cure in place adhesive consisting of:

5-70 wt % of a bodying component including a pre-polymerized (meth)acrylic backbone base polymer having a molecular weight (Mw) of 5,000 to 1,000,000;

0-40 wt % of at least one structural diluent;

30-95 wt % of at least one radical addition diluent;

0-10.0 wt % curative;

0-10 wt % photoinitiator;

0-10 wt % photosensitizer; and

0-10 wt % stabilizer,

wherein the radical addition diluent is selected from the group consisting of epoxy acrylate monomer (ACE™ hydroxyl acrylate), isostearyl acrylate, heptadecyl acrylate, dicyclopentadiene acrylate, 3-ethyl-3-(methyl acrylate) oxetane (OXE-10), 3-ethyl-3-(methyl methacrylate) oxetane (OXE-30), 3,4-epoxycyclohexyl methyl methacrylate (S-100), acrylic macromer having a molecular weight (Mw) of less than 10,000 daltons, 2-acryloyloxypropyl phthalate (V2100), 1,2-cyclohexanedicarboxylic acid, mono[1-methyl-2-[(1-oxo-2-propenyl)oxy]ethyl] ester (cycloaliphatic V2100), polyalkyl methacrylate (PAMA), alkoxylated tetrahydrofurfuryl (THF) acrylate of the following formula (1), hydroxyethyl acrylate of the following formula (2), phenoxyethylacrylate of the following formula (3), tetrahydrofurfuryl acrylate (THFA or THF acrylate) of the following formula (4), and urethane acrylates having a molecular weight (Mw) of less than 2000 daltons,

13. The adhesive of claim 12 further comprising at least one structural diluent, wherein the structural diluent is selected from the group consisting of 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexanecarboxylate (S-21), Bis[(3,4-epoxycyclohexyl)methyl]adipate (S-28), difunctional bisphenol A/epichlorohydrin derived liquid epoxy resin (Epon 828), Bisphenol A epoxy resin having a weight per epoxide of 235-263 g/eq as measured by ASTM D1652 (Epon 834), beta-(3,4-epoxycyclohexyl)ethyltrimethoxysilane (A-186), gamma-glycidoxypropyltrimethoxysilane (A-187), glycidyl ester of neodecanoic acid (EP-10), isocyanate-functional urethane acrylate (Desmolux D100), isocyanate-bearing urethane acrylate (Desmolux D200), aliphatic polyisocyanate (low-viscosity hexamethylene diisocyanate (HDI) biuret) (Desmodur N3200), aliphatic polyisocyanate (hexamethylene diisocyanate (HDI) biuret) (Desmodur N100), aliphatic polyisocyanate (hexamethylene diisocyanate (HDI) trimer) (Desmodur N3300), poly(propylene oxide) (PPO) oligomer having a molecular weight (Mw) of less than 5,000 daltons, trimethylolpropane oxetane (TMPO), poly(ethylene oxide) (PEO) oligomer having a molecular weight (Mw) of less than 5,000 daltons, ethyl hexyl oxetane (2EH oxetane), difunctional oxetane, trimethylolpropane triacrylate (TMPTA) of the following formula (5), tripropyleneglycol diacrylate (TPGDA) of the following formula (6), ethoxylated bisphenol A diacrylate of the following formula (7) in which n+m=3, ethoxylated trimethylolpropane triacrylate of the following formula (8), bisphenol A diglycidyl ether diacrylate of the following formula (9), 1,2-cyclic ethers, 1,3-cyclic ethers, 1,4-cyclic ethers, anhydrides, lactones, lactams, cyclic ethers, siloxanes, oxazolines, oxalidines, and bismaleimides;

14. The adhesive of claim 1 wherein the bodying component includes an acrylic block base polymer, the acrylic block base polymer including two functional end segments and one non-reactive middle segment.

15. The adhesive of claim 14 wherein the non-reactive segment is non-reactive with the reactive functional group of the reactive segments.

16. The adhesive of claim 14 wherein the reactive segments include one or more monomers of the non-reactive segment.

17. The adhesive of claim 1 wherein the bodying component includes an acrylic block base polymer, the acrylic block base polymer including one functional end segment and one non-reactive middle segment.

18. The adhesive of claim 17 wherein the non-reactive segment is non-reactive with the reactive functional group of the reactive segment.

19. The adhesive of claim 17 wherein the reactive segment includes one or more monomers of the non-reactive segment.