Polymer composition comprising a blend of a multimodal polyethylene and a further ethylene polymer suitable for the production of a drip irrigation pipe

1. A polymer composition comprising

(A) a polymer base resin comprising

(A-1) a multimodal ethylene polymer having a density of 930 kg/m 3 or less, and

(A-2) a further ethylene polymer which is other than the multimodal ethylene polymer (A-1) and includes at least

(A-2-b) ethylene polymer produced in a high pressure polymerization process in the presence of a radical initiator, or mixtures thereof,

wherein the amount of the multimodal ethylene polymer (A-1) is 65 wt % to 96 wt % and the amount of the ethylene polymer (A-2) is 4 wt % to 35 wt %, based on the total amount of the polymer base resin (A); and

(B) carbon black;

wherein the polymer composition has a MFRs of 1.5 g/10 min to 10 g/10 min; and wherein the ethylene polymer (A-2) is a mixture of ethylene polymer (A-2-a), which is produced in the presence of a coordination catalyst, and ethylene polymer (A-2-b), wherein the weight ratio of ethylene polymer (A-2-a) and ethylene polymer (A-2-b) is from 97:3 to 3:97.

2. The polymer composition according to claim 1 , wherein the ethylene polymer (A-2) is a mixture of ethylene polymer (A-2-b) which is LDPE and of the ethylene polymer (A-2-a) which is HDPE homo or copolymer of ethylene.

3. A drip irrigation pipe provided with perforations in the pipe wall for discharging water, which perforations are arranged at intervals along the length of the pipe, wherein the pipe comprises a polymer composition as defined in claim 1 .

4. The pipe according to claim 3 , wherein the pipe is provided with emitters arranged at the location of the perforation for controlling the water discharge from the perforation.

5. The pipe according to claim 3 having a diameter of 35 mm or less and a wall thickness of less than 3 mm.

6. The pipe according to claim 3 , wherein the pipe is produced using an in-line process and has a cross-section of round shape or ellipse shape, and wherein the pipe comprises emitters with cylindrical or flat rectangular shape.

7. The polymer composition of claim 1 , that is in the form of pellets.

8. A process for producing a drip irrigation pipe, comprising the steps of

providing a polymer composition comprising

(A) a polymer base resin comprising

(A-1) a multimodal ethylene polymer having a density of 930 kg/m 3 or less, and

(A-2) a further ethylene polymer which is other than the multimodal ethylene polymer (A-1) and includes at least

(A-2-b) ethylene polymer produced in a high pressure polymerization process in the presence of a radical initiator, or mixtures thereof,

wherein the amount of the multimodal ethylene polymer (A-1) is 65 wt % to 96 wt % and the amount of the ethylene polymer (A-2) is 4 wt % to 35 wt %, based on the total amount of the polymer base resin (A); and

(B) carbon black;

wherein the polymer composition has a MFRs of 1.5 g/10 min to 10 g/10 min; and wherein the ethylene polymer (A-2) is a mixture of ethylene polymer (A-2-a), which is produced in the presence of a coordination catalyst, and ethylene polymer (A-2-b), wherein the weight ratio of ethylene polymer (A-2-a) and ethylene polymer (A-2-b) is from 97:3 to 3:97;

mixing the polymer composition in a mixer to form a melt mixture of the polymer composition;

forming the obtained melt mixture of the polymer composition into a form of a pipe having a wall; and

punching perforations at intervals along the length of the formed pipe wall for discharging water from the punched perforations.

9. The process according to claim 8 , wherein the process comprises steps of

providing the polymer composition in the form of pellets;

mixing said pellets of the polymer composition in a mixer to form the melt mixture of the polymer composition;

forming the obtained melt mixture of polymer composition into the form of the pipe; and

punching perforations at intervals along the length of the formed pipe wall for discharging water from the punched perforations.

10. The process according to claim 8 which is an in-line process further comprising the steps of

inserting emitters at intervals into an inner pipe wall along the length of the pipe at time of the formation of said pipe shape; and

punching perforations into the formed pipe wall at the location of the inserted emitter, for discharging water from the punched perforation through said inserted emitter.

11. The process according to claim 8 which is an in-line process comprising the steps of

providing the polymer composition in the form of pellets;

mixing the pellets of polymer composition in a mixer to form a melt mixture of the polymer composition;

forming the obtained melt mixture of polymer composition into the form of the pipe;

inserting emitters at intervals into an inner pipe wall along the length of the pipe at time of the formation of said pipe shape; and

punching perforations to the formed pipe wall at the location of the inserted emitter, for discharging water from the punched perforation through said inserted emitter.

12. The polymer composition according to claim 1 , wherein the ethylene polymer (A-2-a) is produced in the presence of a Ziegler-Natta catalyst system and selected from linear low density copolymer of ethylene (LLDPE) having a density from 918 and up to 930 kg/m 3 , medium density copolymer of ethylene (MDPE) having a density more than 930 and less than 950 kg/m 3 , and high density homopolymer or copolymer of ethylene (HDPE) having a density from 950 to 978 kg/m 3 or from a mixture thereof.