Synthesis of chlorotrifluoroethylene-based block copolymers by iodine transfer polymerization
View Patent ↗Methods for the synthesis of CTFE-based block copolymers through iodine transfer polymerization are disclosed. In an exemplary embodiment, a method includes reacting a fluoromonomer “M” with a chain transfer agent of the formula X—Y or Y—X—Y, wherein X represents a C 1 -C 3 hydrocarbon, a C 1 -C 6 hydrofluorocarbon, C 1 -C 6 hydrochlorofluorocarbon, or C 1 -C 6 fluorocarbon and Y represents iodine or bromine, in the presence of a radical initiator, to form a macro-initiator of the formula: X-poly(M)-Y or Y-poly(M)-X-poly(M)-Y, wherein poly(M) represents a polymer of the fluoromonomer. The method further includes reacting the macro-initiator with chlorotrifluoroethylene (CTFE) in the presence of a radical initiator to form a diblock or a triblock CTFE-based block copolymer of the formula: X-poly(M)-block-poly(CTFE) or PCTFE-block-poly(M)-X-poly(M)-block-PCTFE.
1. A method for the synthesis of CTFE-based block copolymers through iodine transfer polymerization, comprising:
reacting, in the presence of a radical initiator, a monomer “M” selected from the group consisting of: vinyl fluoride (VF), and vinylidene chloride (VDC) with a chain transfer agent of the formula:
X—Y or Y—X—Y,
wherein X represents a C 1 -C 3 hydrocarbon, a C 1 -C 6 hydrofluorocarbon, a C 1 -C 6 hydrochlorofluorocarbon, or a C 1 -C 6 fluorocarbon and Y represents iodine or bromine, thereby forming a macro-initiator of the formula:
X-poly(M)-Y or Y-poly(M)-X-poly(M)-Y,
wherein poly(M) represents a polymer of the monomer; and
reacting, in the presence of a radical initiator, the macro-initiator with chlorotrifluoroethylene (CTFE), thereby forming a diblock or a triblock CTFE-based block copolymer of the formula:
X-poly(M)-block-PCTFE or PCTFE-block-poly(M)-X-poly(M)-block-PCTFE.
2. The method of claim 1 , wherein reacting the monomer with the chain transfer agent comprises reacting the monomer with a chain transfer agent selected from the group consisting of: CF 3 (CF 2 ) n —Y and Y—(CF 2 ) n —Y, wherein n equals 0, 1, 2, 3, 4, 5, or 6.
3. The method of claim 1 , wherein reacting the monomer with the chain transfer agent in the presence of the radical initiator comprises reacting the monomer with a chain transfer agent in the presence of a radical initiator selected from the group consisting of: (NH 4 ) 2 S 2 O 8 , K 2 S 2 O 8 , Na 2 S 2 O 8 , Mn 2 (CO) 10 , tertbutyl peroxypivalate, dibenzoyl peroxide, and ditert-butyl peroxide.
4. The method of claim 1 , wherein reacting the monomer with the chain transfer agent comprises reacting the monomer with the chain transfer agent at a temperature of about 20° C. to about 130° C.
5. The method of claim 4 , wherein reacting the monomer with the chain transfer agent comprises reacting the monomer with the chain transfer agent at a temperature of about 60° C. to about 100° C.
6. The method of claim 1 , wherein reacting the monomer with the chain transfer agent comprises reacting the monomer with the chain transfer agent at a pressure of about 200 kPa to about 20,000 kPa.
7. The method of claim 6 , wherein reacting the monomer with the chain transfer agent comprises reacting the monomer with the chain transfer agent at a pressure of about 2,000 kPa to about 10,000 kPa.
8. The method of claim 1 , wherein reacting the monomer with the chain transfer agent comprises reacting the monomer with the chain transfer agent for a time period of about 1 to about 30 hours.
9. The method of claim 8 , wherein reacting the monomer with the chain transfer agent comprises reacting the monomer with the chain transfer agent for a time period of about 4 to about 20 hours.
10. The method of claim 1 , wherein reacting the macro-initiator with the CTFE in the presence of a radical initiator comprises reacting the macro-initiator with the CTFE in the presence of a radical initiator selected from the group consisting of: Mn 2 (CO) 10 and tert-butyl peroxy pivalate (TBPPi).
11. The method of claim 1 , wherein reacting the macro-initiator with the CTFE comprises reacting the macro-initiator with the CTFE at a temperature of about 20° C. to about 130° C.
12. The method of claim 11 , wherein reacting the macro-initiator with the CTFE comprises reacting the macro-initiator with the CTFE at a temperature of about 60° C. to about 100° C.
13. The method of claim 1 , wherein reacting the macro-initiator with the CTFE comprises reacting the macro-initiator with the CTFE at a pressure of about 200 kPa to about 20,000 kPa.
14. The method of claim 1 , wherein reacting the macro-initiator with the CTFE comprises reacting the macro-initiator with the CTFE for a time period of about 1 to about 30 hours.
15. The method of claim 1 , wherein reacting the monomer or the macro-initiator comprises reacting in a solvent selected from the group consisting of: esters of formula R—COOR′ where R and R′ are independently C 1-5 alkyl groups, ester OR″ where R″ is an alkyl containing 1 to 5 carbon atoms, and where R may also hydrogen, fluorinated solvents, 1,2-dichloroethane, isopropanol, tertiary butanol, acetonitrile, dimethyl carbonate, butyronitrile, and mixtures thereof.
16. The method of claim 15 , wherein reacting the monomer or the macro-initiator comprises reacting in a co-solvent selected from the group consisting of: acetonitrile, butyronitrile, alkyl ketones, cyclohexanone, and water.
17. The method of claim 1 , wherein the monomer “M” comprises vinyl fluoride (VF).
18. The method of claim 1 , wherein the monomer “M” comprises vinylidene chloride (VDC).