Heat resistant titanium alloy sheet excellent in cold workability and a method of production of the same
View Patent ↗The present invention provides a heat resistant titanium alloy sheet excellent in cold workability having high temperature strength characteristics better than JIS Class 2 pure titanium and having a cold workability and high temperature oxidation resistance equal to or better than that of JIS Class 2 pure titanium and a method of production of the same, that is, a heat resistant titanium alloy sheet excellent in cold workability characterized by comprising, by mass %, 0.3 to 1.8% of Cu, 0.18% or less of oxygen, 0.30% or less of Fe, and, as needed, at least one of Sn, Zr, Mo, Nb, and Cr in a total of 0.3 to 1.5%, and the balance of Ti and less than 0.3% of impurity elements and by a β-phase and Ti 2 Cu-phase being included in a volume percentage of 0 to 2% and, further, a method of production of that titanium alloy sheet characterized by performing the final annealing at 630 to 850° C. in temperature range or performing the hot-rolled sheet or coil annealing or intermediate annealing at 630 to 850° C. in temperature range and perform the final annealing after cold working at 600 to 630° C. in temperature.
1. A heat resistant titanium alloy sheet excellent in cold workability comprising, by mass %, 0.3 to 1.8% of Cu, 0.18% or less of oxygen, 0.30% or less of Fe, and a balance of Ti and less than 0.3% of impurity elements, and further comprising a β-phase and Ti 2 Cu-phase in total having a volume percentage of 2%, and a balance of an α-phase,
wherein said titanium alloy sheet further contains at least one or more of Sn, Zr, Mo, Nb, and Cr in a total of 0.3 mass % to 1.5 mass %.
2. A heat resistant titanium alloy sheet excellent in cold workability comprising, by mass %, 0.3 to 1.8% of Cu, 0.18% or less of oxygen, 0.30% or less of Fe, and a balance of Ti and less than 0.3% of impurity elements, and further comprising a β-phase and Ti 2 Cu-phase in total having a volume percentage of 0.1% or less and a balance of an α-phase,
wherein said titanium alloy sheet further contains at least one or more of Sn, Zr, Mo, Nb, and Cr in a total of 0.3 mass % to 1.5 mass %.