Cable components formed with a thermoplastic elastomer as a nucleating agent
View Patent ↗Components for incorporation into cable, such as communication cables, are described. At least one cable component, such as an optical fiber buffer tube, may be formed from a polymeric resin that has been nucleated or otherwise combined with a thermoplastic elastomer. The cable component may then be incorporated into a cable that includes at least one transmission element.
1. A communications cable comprising:
at least one transmission element; and
at least one component at least partially formed form a polymeric resin, the polymeric resin comprising:
a base polymeric material; and
a nucleating agent comprising a thermoplastic elastomer, the nucleating agent comprising between approximately one percent and approximately thirty percent by weight of the polymeric resin.
2. The communications cable of claim 1 , wherein the at least one transmission element comprises at least one optical fiber, and
wherein the at least one component comprises one of (i) a buffer tube formed around the at least one optical fiber or (ii) a tight buffer formed around the at least one optical fiber.
3. The communications cable of claim 1 , wherein the at least one transmission element comprises a plurality of twisted pairs of conductors, and
wherein the at least one component comprises a separator positioned between at least two of the plurality of twisted pairs of conductors.
4. The communications cable of claim 1 , wherein the at least one component comprises a jacket formed around the at least one transmission element.
5. The communications cable of claim 1 , wherein the base polymeric material comprises polypropylene.
6. The communications cable of claim 1 , wherein the base polymeric material comprises one of (i) a polypropylene homopolymer or (ii) a polypropylene copolymer that comprises ethylene.
7. The communications cable of claim 1 , wherein the thermoplastic elastomer comprises one of (i) a styrenic block copolymer, (ii) a polyolefin blend, (iii) an elastomeric alloy, (iv) a thermoplastic polyurethane, (v) a thermoplastic copolyester, or (vi) a thermoplastic polyamide.
8. The communications cable of claim 1 , wherein the thermoplastic elastomer comprises one of (i) styrene-butadiene-styrene (SBS) or styrene-ethylene-butene-styrene (SEBS).
9. The communications cable of claim 1 , wherein the thermoplastic elastomer comprises a two phase structure, the structure comprising a continuous phase that exhibits elastic behavior and a dispersed phase that provides physical cross-linking.
10. The communications cable of claim 1 , wherein the thermoplastic elastomer comprises a first material that contributes to mixing with the base polymeric material and a second material that promotes nucleation of the base polymeric material.
11. The communications cable of claim 1 , wherein the polymeric resin further comprises a compatabilizer that promotes mixing of the base polymeric material and the thermoplastic elastomer.
12. The communications cable of claim 1 , wherein the polymeric resin further comprises a cross-linking agent that promotes chemical cross-linking of the base polymeric material and the thermoplastic elastomer.
13. The communications cable of claim 1 , wherein the polymeric resin comprises between approximately three percent and approximately ten percent by weight of the thermoplastic elastomer as a nucleating agent.
14. The communications cable of claim 1 , wherein the polymeric resin comprises between approximately 0.3 percent and approximately 9.0 percent by weight of a dispersed phase component of the thermoplastic elastomer.
15. The communications cable of claim 1 , wherein the polymeric resin further comprises at least one of (i) a flame retardant material or (ii) a low smoke zero halogen material.
16. The communications cable of claim 1 , wherein the polymeric resin further comprises at least one of (i) a smoke suppressant, (ii) an antioxidant, (iii) a plasticizer, (iv) a reinforcing filler material, (v) an ultraviolet stabilizer, (vi) a moisture absorbing material, (vii) a moisture blocking material, (viii) a slip agent, (ix) a coefficient of friction reducing material, (x) a colorant, or (xi) a foaming agent.
17. An optical fiber cable comprising:
at least one optical fiber; and
a buffer element formed around the at least one optical fiber, the buffer element at least partially formed from a polymeric resin comprising:
a base polymeric material; and
a nucleating agent comprising a thermoplastic elastomer, the nucleating agent comprising between approximately one percent and approximately thirty percent by weight of the polymeric resin.
18. The optical fiber cable of claim 17 , wherein the buffer element comprises one of (i) a buffer tube or (ii) a tight buffer.
19. A buffer tube for use in an optical fiber cable, the buffer tube comprising:
a polymeric resin formed into a tube, the polymeric resin comprising a base polymeric material and a nucleating agent comprising a thermoplastic elastomer combined with the base polymeric material, the nucleating agent comprising between approximately one percent and approximately thirty percent by weight of the polymeric resin.
20. A method for forming a component of a communications cable, the method comprising:
providing a polymeric resin comprising at least one polymeric material;
nucleating the polymeric resin by combining a thermoplastic elastomer with the polymeric resin, wherein the thermoplastic elastomer comprises between approximately one percent and approximately thirty percent by weight of the nucleated polymeric resin; and
extruding the nucleated polymeric resin to form the component of the communications cable.
21. The method of claim 20 , wherein extruding the nucleated polymeric resin comprises extruding the nucleated polymeric resin to form one of (i) an optical fiber buffer tube or (ii) an optical fiber tight buffer.