Metal nanowire inks for the formation of transparent conductive films with fused networks
Fusing nanowire inks are described that can also comprise a hydrophilic polymer binder, such as a cellulose based binder. The fusing nanowire inks can be deposited onto a substrate surface and dried to drive the fusing process. Transparent conductive films can be formed with desirable properties.
1. A metal nanowire ink comprising aqueous solvent, from about 0.001 wt % to about 4 wt % metal nanowires, from about 0.05 wt % to about 5 wt % solid hydrophilic polymer binder soluble in the solvent, and from about 0.0001 to about 0.5 wt % metal ions provided to the ink as a dissolved fusing solution, having from about 5 wt % to about 60 wt % ethanol in the aqueous solvent.
2. The metal nanowire ink of claim 1 wherein the hydrophilic polymer binder comprises a polymeric polyol.
3. The metal nanowire ink of claim 1 wherein the hydrophilic polymer binder comprises a polysaccharide.
4. The metal nanowire ink of claim 1 wherein the hydrophilic polymer binder comprises a cellulose based polymer or chitosan based polymer.
5. The metal nanowire ink of claim 1 comprising from about 0.01 wt % to about 2 wt % metal nanowires comprising silver nanowires, from about 0.1 wt % to about 2 wt % hydrophilic polymer binder comprising a polysaccharide polymer binder, and from about 0.001 to about 0.2 wt % metal ions comprising silver ions.
6. The metal nanowire ink of claim 1 comprising from about 0.01 wt % to about 2 wt % metal nanowires comprising silver nanowires, from about 0.1 wt % to about 2 wt % hydrophilic binder comprising a polysaccharide binder, and from about 0.001 to about 0.2 wt % metal ions selected from the groups consisting of silver, gold, platinum, palladium, zinc, nickel and combinations thereof.
7. The metal nanowire ink of claim 1 having a pH at least about 3 pH units.
8. The metal nanowire ink of claim 1 having a pH from about 5.5 to about 7.5 pH units.
9. The metal nanowire ink of claim 1 wherein no visible settling can be observed after one hour of sitting without stirring.
10. The metal nanowire ink of claim 1 further comprising from about 0.01 wt % to about 2.5 wt % curable binder.
11. A metal nanowire ink comprising an aqueous solvent, from about 0.001 wt % to about 4 wt % silver nanowires, from about 0.0001 to about 0.5 wt % metal ions provided to the ink as a dissolved fusing solution, anions selected from the group consisting of nitrates, sulfates, perchlorates, acetates, fluorides, chlorides, bromides, and iodides, and from about 10 wt % to about 60 wt % ethanol in the aqueous solvent at a pH from about 5.5 to about 7.5 pH units.
12. A metal nanowire ink comprising from about 0.001 wt % to about 4 wt % metal nanowires, from about 0.05 wt % to about 5 wt % hydrophilic polymer binder, from about 0.0001 to about 0.5 wt % metal ions provided to the ink as a dissolved fusing solution, and from about 5 wt % to about 60 wt % ethanol in an aqueous solvent, wherein the hydrophilic polymer binder comprises a polymeric polyol.
13. The metal nanowire ink of claim 12 wherein the hydrophilic polymer binder comprises a polysaccharide.
14. The metal nanowire ink of claim 12 wherein the hydrophilic polymer binder comprises a cellulose based polymer or chitosan based polymer.
15. The metal nanowire ink of claim 12 comprising from about 0.01 wt % to about 2 wt % metal nanowires comprising silver nanowires, from about 0.1 wt % to about 2 wt % hydrophilic binder comprising a polysaccharide polymer binder, and from about 0.001 to about 0.2 wt % metal ions selected from the groups consisting of silver, gold, platinum, palladium, zinc, nickel and combinations thereof.
16. The metal nanowire ink of claim 12 having a pH at least about 3 pH units.
17. The metal nanowire ink of claim 12 having a pH from about 5.5 to about 7.5 pH units.
18. The metal nanowire ink of claim 12 wherein no visible settling can be observed after one hour of sitting without stirring.