Stepwise interfacial polymerization technique with different reagent solution designs to prepare hollow fiber nanofiltration membrane composites
View Patent ↗Novel low-pressure nanofiltration membrane composites for rejecting organic compounds are prepared by interfacial polymerization on a microporous hollow fiber supporting membrane. The interfacial polymerization reaction is carried out using an essentially monomeric polyamine reactant having at least two amine functional groups per molecule, and an essentially monomeric amine-reactive polyfunctional aromatic or cycloaliphatic acyl halide having at least two acyl halide groups per molecule. The composite can be fabricated by stepwise polymerization reactions with different reactant recipes at each step.
1. A method for fabricating a hollow fiber nanofiltration (NF) membrane composite comprising:
providing at least one hollow fiber ultrafiltration (UF) membrane;
injecting a first monomeric polyamine reactant into at least one hollow channel of the hollow fiber UF membrane;
injecting a first monomeric amine-reactive polyfunctional aromatic or cycloaliphatic acyl halide into the hollow channel of the hollow fiber UF membrane to react with the first monomeric polyamine reactant to form a polymer layer on an inner surface of the hollow fiber UF membrane through a first interfacial polymerization;
injecting a second monomeric polyamine reactant into the hollow channel of the hollow fiber UF membrane; and
injecting a second monomeric amine-reactive polyfunctional aromatic or cycloaliphatic acyl halide into the hollow channel of the hollow fiber UF membrane to react with the second monomeric polyamine reactant to form a NF-functionalized layer on the polymer layer through a second interfacial polymerization,
wherein said first monmeric polyamine reactant comprises polyethyleneimine (PEI) with a molecular weight of 40,000 Da at a concentration of 0.1-0.5 wt. % and piperazine (PIP) at a concentration of 0.05-0.2 wt. % dissolved in water and said second monomeric polyamine reactant comprises 1,3-phenylenediamine (MPD) at a concentration of 0.05-0.2 wt % and sodiumdodecylsulfate (SDS) at a concentration of 0.1 wt. % dissolved in water.
2. The method of claim 1 , wherein the first and the second monomeric amine-reactive polyfunctional aromatic or cycloaliphatic acyl halide contain at least about two acyl halide groups per molecule.
3. The method of claim 1 , further comprising curing the polymer layer at 50-80° C. for 1-5 hr after the first interfacial polymerization.
4. The method of claim 1 , further comprising curing the NF-functionalized layer at 50-80° C. for 1-5 hr after the second interfacial polymerization.
5. The method of claim 1 , wherein the first and/or the second monomeric amine-reactive polyfunctional aromatic or cycloaliphatic acyl halide comprises trimesoylchloride (TMC) at a concentration of 0.1 wt. % dissolved in hexane.
6. A hollow fiber nanofitration membrane composite fabricated by the method of claim 1 .
7. The hollow fiber nanofitration membrane composite of claim 6 , wherein a NF membrane product comprising the hollow fiber NF membrane composite provides at least 80% rejection rate for compounds having a molecular weight at 400 Da and a water flux value of 8-20 L/m 2 hr under a driving pressure range of 0.2-0.4 MPa.
8. The hollow fiber nanofitration membrane composite of claim 6 , wherein a NF membrane product comprising the hollow fiber NF membrane composite works at a pH range of 2-10 with a rejection rate higher than 80% for compounds having a molecular weight of 400 Da.
9. A hollow fiber nanofitration membrane composite comprising:
a hollow fiber UF membrane comprising polyvinylidene fluoride (PVDF);
a polymer layer formed on the inner surface of the hollow fiber UF membrane, and comprising a first cross-linked aromatic polyamides, wherein the first cross-linked aromatic polyamides is formed by reacting a first monomeric polyamine reactant comprising PEI having a molecular weight of 40,000 Da at a concentration of 0.1-0.5 wt. % dissolved in water with a solution of TMC in hexane at a concentration of 0.1 wt. %; and
a NF-functionalized layer formed on the polymer layer, and comprising a second cross-linked aromatic polyamides, wherein the second cross-linked aromatic polyamides is formed by reacting a second monomeric polyamine reactant comprising MPD at a concentration of 0.05-0.2 wt % and SDS at a concentration of 0.1 wt. % dissolved in water with a solution of TMC in hexane at a concentration of 0.1 wt. %.
10. A system for performing the method of claim 1 , comprising:
a reactant tank for holding reactants;
a membrane module for holding the hollow fiber UF membrane;
a tube for transporting the reactants; and
a pump for injecting the reactants into the hollow fiber UF membrane.
11. The method of claim 1 , wherein the hollow fiber UF membrane comprises polyvinylidene fluoride (PVDF).