Process for smoothing the surface of a part made of CMC material
View Patent ↗A method of smoothing the surface of a ceramic matrix composite material part that presents a surface that is undulating and rough. The method includes depositing a refractory vitreous coating on the surface of the part, the vitreous coating essentially containing silica, alumina, baryte, and lime.
1. A method of smoothing the surface of a ceramic matrix composite material part that presents a surface that is undulating and rough, the method comprising depositing a refractory vitreous coating on the surface of the part, the vitreous coating comprising silica, alumina, BaO, and lime, and wherein the vitreous coating comprises, in percentages by weight, 55% to 70% of silica, 5% to 20% of alumina, 5% to 15% of BaO and 5% to 10% of lime.
2. A method according to claim 1 , further comprising, prior to depositing the vitreous coating on the surface of the part, forming a ceramic coating made by applying a liquid composition to the surface of the part, the liquid composition containing a ceramic precursor polymer and a solid refractory filler, curing the polymer, and transforming the cured polymer into ceramic by heat treatment.
3. A method according to claim 1 wherein the part comprises carbon fiber reinforcement densified by a silicon carbide matrix.
4. A method according to claim 1 , wherein the part comprises carbon fiber reinforcement densified by a silicon-based matrix.
5. A method according to claim 1 , wherein the vitreous coating also contains at least one additional compound selected at least from an alkaline-earth oxide and an alkali oxide.
6. A method according to claim 1 , wherein the vitreous coating presents a coefficient of thermal expansion departing by no more than ±0.5×10 −6 K −1 from the coefficient of thermal expansion of the CMC material of the part.
7. A method according to claim 1 , wherein the vitreous coating presents a melting temperature greater than or equal to 1300° C.
8. A method according to claim 1 , wherein the vitreous coating is deposited on the part by plasma spraying or oxy-acetylene flame spraying.
9. A method according to claim 1 , wherein the vitreous coating is deposited on the part by coating, with heat treatment of the deposited coating being performed subsequently.
10. A method according to claim 1 , wherein the ceramic matrix composite material part is a gas turbine blade.