Multi-region battery separators
Disclosed is a battery separator, comprising two fiber regions comprising glass fibers, and a middle fiber region disposed between them comprising larger average diameter fibers and specified amounts of silica, or fine fibers, or both; and processes for making the separator. Also disclosed is a battery separator, comprising a fiber region and either one or two silica-containing region(s) adjacent thereto, each of the regions containing a specified amount of silica; and processes for making the separator. Such separators are useful, e.g., in lead-acid batteries.
1. A battery separator, comprising:
a fiber region; and
either
(a) a silica-containing region adjacent to the fiber region, or
(b) a first silica-containing region and a second silica-containing region, wherein the fiber region is disposed between the first silica-containing region and the second silica-containing region;
wherein the fiber region and each silica-containing region contains fibers having an average diameter from about 2 to about 25 μm;
wherein the fiber region contains less than 2% by weight silica; and
wherein each silica-containing region independently contains greater than or equal to 2% by weight silica.
2. The battery separator according to claim 1 , wherein each silica-containing region independently contains 2 to about 30% by weight silica.
3. The battery separator according to claim 1 , wherein the thickness of the fiber region constitutes greater than or equal to 25% of the total separator thickness, and the thickness of the silica-containing region(s) constitutes greater than or equal to 30% of the total separator thickness.
4. A lead-acid battery comprising a negative plate, a positive plate, and a battery separator according to claim 1 , wherein the battery separator is disposed between the negative and positive plates.
5. The battery separator according to claim 1 , wherein the fiber region comprises fibers having an average diameter from about 3 to about 15 μm.
6. The battery separator according to claim 1 , wherein the fiber region comprises glass fibers having an average diameter from about 3 to about 15 μm.
7. The battery separator according to claim 1 , wherein the fiber region comprises glass fibers having an average diameter from about 0.4 to about 1.8 μm.
8. The battery separator according to claim 1 , wherein the thickness of the fiber region constitutes 10-40% of the total separator thickness.
9. The battery separator according to claim 1 , wherein the fiber region comprises from about 5 to about 50% by weight glass fibers having an average diameter from about 0.1 to less than 2 μm.
10. The battery separator according to claim 1 , wherein the fiber region comprises from about 5 to about 50% by weight glass fibers having an average diameter from about 0.8 to about 1.6 μm.
11. The battery separator according to claim 1 comprising a first silica-containing region and a second silica-containing region, each silica-containing region comprising glass fibers, wherein the average glass fiber diameter of the first silica-containing region differs from the average glass fiber diameter of the second silica-containing region by greater than or equal to 0.5 μm.
12. The battery separator according to claim 11 , wherein each of the silica-containing regions comprises from about 2 to about 40% by weight silica, and wherein the specific surface area of each of the silica-containing regions is from about 1 to about 300 m 2 /g.
13. The battery separator according to claim 1 , wherein the fiber region comprises from about 1 to about 40% by weight glass fibers having an average diameter from about 0.1 to less than 2 μm, and wherein the specific surface area of the fiber region is from about 1 to about 25 m 2 /g.
14. The battery separator according to claim 1 , wherein the fiber region comprises from about 1 to 50% by weight glass fibers having an average diameter from about 0.1 to less than 2 μm, and wherein the tensile strength (machine direction) of the separator is about 2.00 to about 2.40 lbs/inch and/or the tensile strength (cross direction) of the separator is about 1.75 to about 2.20 lbs/inch.
15. The battery separator according to claim 1 , wherein the separator exhibits an acid filling time of about 17 to about 155 seconds.
16. The battery separator according to claim 1 , wherein the separator exhibits an acid stratification distance from about 2.5 to about 16 cm.
17. The battery separator according to claim 1 , wherein the separator exhibits an acid filling time of about 17 to about 50 seconds.
18. The battery separator according to claim 1 , wherein the thickness of the fiber region constitutes 1-49% of the total separator thickness.