STAMPER, METHOD FOR PRODUCING THE SAME, METHOD FOR PRODUCING MOLDED MATERIAL, AND PROTOTYPE ALUMINUM MOLD FOR STAMPER
Disclosed herein are a stamper which has anodized alumina formed on the surface thereof and which will not cause macroscopic unevenness or color unevenness on the transcribed surface; a method for producing the same; and a method for producing a molded material without macroscopic unevenness or color unevenness on the transcribed surface thereof by using such a stamper. The stamper includes alumina which has a microasperity structure and which is formed by anodization on the surface of a prototype aluminum mold having an aluminum purity of 99.5% or more, an average crystal-grain diameter of 1 mm or less, and an arithmetic mean surface roughness Ra of 0.05 μm or less. The use of this stamper enables the production of a molded material which does not have macroscopic unevenness or color unevenness on the transcribed surface thereof and which is suitable for use as an antireflection article and the like.
1 . A method for producing a stamper having alumina having a microasperity structure formed on a surface thereof, the method comprising:
(a) a forging step of applying a forge treatment to an aluminum material to obtain a prototype aluminum mold having a substantially roll shape, wherein the processing direction is changed in the forging treatment
(b) a first oxide coating film forming step of forming an oxide coating film by anodizing a prototype aluminum mold in an electrolytic solution and at a constant voltage;
(c) an oxide coating film removing step of removing the oxide coating film thus formed to form pore generating points for anodization;
(d) a second oxide coating film forming step of reanodizing an intermediate aluminum mold having the pore generating points formed thereon in an electrolytic solution and at a constant voltage to form an oxide coating film having pores at the pore generating points; and
(e) a pore diameter enlarging step of enlarging the diameters of the pores thus formed,
wherein the prototype aluminum mold has an average crystal-grain diameter of 1 mm or less and an arithmetic mean surface roughness Ra of 0.05 μm or less.
2 . The method for producing the stamper according to claim 1 , wherein the height difference of the unevenness due to the crystal grain boundary on the surface of the stamper is 600 nm or less.
3 . The method for producing the stamper according to claim 1 , wherein the microasperity structure of the stamper includes pores whose aspect ratio is 1.8 or more.