Glass sheet capable of being inhibited from warping through chemical strengthening
View Patent ↗A glass sheet has one surface and the other surface facing the one surface in a thickness direction, wherein a fluorine concentration (average fluorine concentration by SIMS at a depth of 1 to 24 μm) in the one surface is higher than that in the other surface. The following expression is satisfied: 0.07≦ΔF/ΔH 2 O. ΔF (mol %) is a value obtained by subtracting an average fluorine concentration in the surface having the lower fluorine concentration from that in the surface having the higher fluorine concentration, and ΔH 2 O (mol %) is an absolute value of a value obtained by subtracting an average H 2 O concentration in the surface having the higher fluorine concentration from that in the surface having the lower fluorine concentration.
1. A glass sheet, having one surface and the other surface facing the one surface in a thickness direction, wherein a fluorine concentration in the one surface is higher than the fluorine concentration in the other surface in which the fluorine concentration is an average fluorine concentration (mol %) by SIMS at a depth of 1 to 24 μm, and the following expression (1) is satisfied:
0.07≦ΔF/ΔH 2 O (1)
wherein ΔF is a value obtained by subtracting an average fluorine concentration (mol %) by SIMS at the depth of 1 to 24 μm in the surface having the lower fluorine concentration from the average fluorine concentration (mol %) by SIMS at the depth of 1 to 24 μm in the surface having the higher fluorine concentration, and
ΔH 2 O is an absolute value of a value obtained by subtracting an average H 2 O concentration (mol %) by SIMS at the depth of 1 to 24 μm in the surface having the higher fluorine concentration from the average H 2 O concentration (mol %) by SIMS at the depth of 1 to 24 μm in the surface having the lower fluorine concentration,
wherein the surface having the higher fluorine concentration does not include a recess having a diameter of 10 nm or more; or wherein the surface having the higher fluorine concentration comprises one or more recesses with a density of 6 recesses/μm 2 or less.
2. The glass sheet according to claim 1 , which is manufactured by a float method.
3. The glass sheet according to claim 1 , which has a thickness of 1.5 mm or less.
4. The glass sheet according to claim 1 , which has a thickness of 0.8 mm or less.
5. A glass sheet, which is obtained by chemically strengthening the glass sheet according to claim 1 .
6. A flat panel display device, comprising a cover glass, wherein the cover glass is the glass sheet according to claim 5 .
7. The glass sheet according to claim 1 , which is prepared by contacting a glass sheet with fluorine wherein the glass sheet has a surface temperature of greater than 650° C.