ADHESIVE COMPOSITIONS WITH AMORPHOUS POLYOLEFINS
The invention relates to a hot melt adhesive composition that, when used as an elastic attachment adhesive (EAA), provides elastic laminates having an initial creep performance of less than 25%. The composition comprises a selectively hydrogenated, high vinyl block copolymer having the structure SEBS or (SEB) n X amorphous polyolefin such as polyethylene, polypropylene, butylene homopolymers and copolymers, or a mixture of two or more of these, tackifier, and maleated polypropylene oligomer or maleated SEBS.
1 . A composition comprising:
a) 10 to 20 wt. % of a selectively hydrogenated block copolymer having the structure SEBS or (SEB) n X wherein S represents a poly(monoalkenyl arene) block, EB represents a hydrogenated polybutadiene block, n is an integer from 2 to about 30 and X is the residue of a coupling agent, and wherein the block copolymer has a vinyl content of greater than 50% before selective hydrogenation and 10 wt. % or less of diblock polymer is present;
b) 40 to 50 wt. % of an amorphous polyolefin;
c) 25 to 35 wt. % of a tackifier; and
d) 3 to 8 wt. % of a maleated polypropylene oligomer or maleated SEBS where the total composition is 100 wt. %.
2 . The composition of claim 1 , wherein S is a polystyrene block.
3 . The composition of claim 2 , wherein said SEBS has polystyrene end blocks with a peak molecular weight of 8 to 12 kg/mol., a total peak block molecular weight of at least 145 kg/mol., a polystyrene content of 15 to 30 wt. %, a vinyl content of at least 60%, and a melt flow rate of less than 12 g/10 min. (230° C./2.16 kg according to ASTM D-1238).
4 . The composition of claim 1 , wherein the vinyl content is from 65 to 75%.
5 . The composition of claim 3 , wherein the polystyrene content is from 18 to 23 wt. %.
6 . The composition of claim 3 , wherein the block copolymer has a peak total molecular weight from 145 to 200 kg/mol.
7 . The composition of claim 3 , wherein said polybutadiene peak molecular weight is 128 to 148 kg/mol.
8 . The composition of claim 3 , wherein the melt flow rate is 1 to 10 g/10 min. (230° C./2.16 kg according to ASTM D-1238).
9 . The composition of claim 1 , wherein said amorphous alpha polyolefin is ethylene, propylene or butylene homopolymers, or ethylene, propylene or butylene copolymers, or mixtures thereof.
10 . The composition of claim 9 , wherein said ethylene, propylene and butylene copolymers may be ethylene/octene or propylene/octene or butylene/octene copolymers.
11 . The composition of claim 1 , wherein said tackifier resin is rosin esters, styrenated terpenes, polyterpenes, terpene phenolics or mixtures of two or more thereof.
12 . The composition of claim 1 , wherein said maleated polypropylene oligomer or maleated SEBS, or a mixture thereof possesses at least 1 wt. % maleation level.
13 . The composition of claim 12 , wherein the maleation level is from 1 to 15 wt. %.
14 . The composition of claim 1 , wherein the block copolymer has the structure (SEB) n X wherein n is from 2 to 4.
15 . The composition of claim 1 , wherein the coupling agent residue results from coupling agents selected from tetra-alkoxysilanes, alkyl-trialkoxysilanes, aliphatic esters, and diglycidyl aromatic epoxy compounds.
16 . The composition of claim 15 , wherein the coupling agent is tetra-ethoxysilane, tetra-methoxysilane, methyl-trimethoxysilane, or mixtures thereof.
17 . An elastic laminate construction comprising the composition of claim 1 .
18 . The laminate of claim 17 , wherein the initial creep is less than 25%.
19 . An article comprising the laminate of claim 17 .
20 . The article of claim 19 , which is a personal hygiene article selected from diapers or adult incontinence articles.