Abrasive particles having a unique morphology
View Patent ↗An abrasive particle having an irregular surface, wherein the surface roughness of the particle is less than about 0.95. A method for producing abrasive particles having a unique surface morphology including providing a plurality of abrasive particles; providing a plurality of metal particles; mixing the abrasive particles and the metal particles to form a mixture; compressing the mixture to form a compressed mixture; heating the compressed mixture; and recovering modified abrasive particles.
1. A method for producing abrasive particles having an irregular surface comprising the steps of:
providing a plurality of abrasive particles;
providing a plurality of metal particles;
mixing said abrasive particles and said metal particles to form a mixture;
compressing said mixture to form a compressed mixture;
heating said compressed mixture;
modifying a surface of the particles; and
recovering the modified abrasive particles, wherein a surface roughness of the modified abrasive particle is less than about 0.95 and the sphericity of said particle is less than about 0.70, each particle having one or more spikes and pits.
2. The method of claim 1 , wherein said compressing step comprises forming said mixture into a pellet.
3. The method of claim 1 , further comprising the step of adding a binder.
4. The method of claim 1 , wherein said abrasive particles are diamond particles.
5. The method of claim 1 , wherein said diamond particles are monocrystalline diamond particles.
6. The method of claim 1 , wherein said metal particles are iron particles.
7. The method of claim 1 , wherein said heating step comprises heating said particles and said metal particles to a temperature of at least about 700° C.
8. The method of claim 1 , wherein the percentage of abrasive particles to metal particles is about 20 wt % to about 80 wt %.
9. The method of claim 1 , wherein said modified abrasive particles have an average weight loss of more than about 5% of the weight loss compared to unprocessed abrasive particles.
10. The method of claim 9 , wherein said modified abrasive particles have an average weight loss of more than about 20% of the weight loss compared to unprocessed abrasive particles.
11. The method of claim 1 , wherein the average size of the metal particles is less than about one half of the diameter of the abrasive particle.
12. The method of claim 1 , wherein said abrasive particles range in size from about 0.1 micron to about 1000 microns.
13. The method of claim 1 , wherein said abrasive particles are cubic boron nitride particles.
14. The method of claim 1 , wherein the sphericity of said particle is between about 0.25 to about 0.6.